摘要
The tensile properties and fracture surface of 07MnNiCrMoVDR steel welded joint at low temperature have been studied by universal testing machine and scanning electron microscope. The results show that the tensile properties of 07MnNiCrMoVDR steel welded joint are greatly affected by temperature. Tensile strength and yield strength of 07MnNiCrMoVDR steel welded joint increase, but elongation and reduction of area decrease with temperature decreasing. The macro-fracture of 07 MnNiCrMoVDR steel welded joint exhibits that the shear lip is not significant and micro-fracture makes up of dimpled fracture and tear fracture, and dimple becomes tiny and uniform with temperature decreasing.
The tensile properties and fracture surface of 07MnNiCrMoVDR steel welded joint at low temperature have been studied by universal testing machine and scanning electron microscope. The results show that the tensile properties of 07MnNiCrMoVDR steel welded joint are greatly affected by temperature. Tensile strength and yield strength of 07MnNiCrMoVDR steel welded joint increase, but elongation and reduction of area decrease with temperature decreasing. The macro-fracture of 07 MnNiCrMoVDR steel welded joint exhibits that the shear lip is not significant and micro-fracture makes up of dimpled fracture and tear fracture, and dimple becomes tiny and uniform with temperature decreasing.