采用AZ31镁合金铸锭在实验室立式等径双辊铸轧机上进行铸轧试验；对铸轧带坯直接进行冷轧和冷轧后退火处理．研究了Az31镁合金薄带立式双辊铸轧工艺及铸轧带坯进行冷轧、轧后退火过程的组织演变行为．采用合理的工艺参数，成功铸轧出镁合金薄带，同时由于双辊铸轧快速冷却和压力下凝固成形技术特点，改善了镁合金的凝固组织．对铸轧镁合金带坯直接进行冷轧，最大变形量可以达到40．7％．经过冷轧后的镁合金板材，在350℃下退火30-60min，可以获得平均晶粒直径为9～10μm的等轴晶细晶组织．
An experiment was carried out magnesium alloy AZ31 ingots as workpiece directly. The parameters in the processes of microstructure evolution of the finished cold in lab on vertical twin-roll casting machine with which were cold rolled to form strip then annealed vertical twin-roll cast-rolling and annealing, and the strip were investigated. The results showed that the magnesium alloy strip is obtained successfully due to reasonable process parameters, especially in the twin-roll cast-rolling process both the quick chilling and pressured solidification improve the solidified structure of the strip of which the maximum deformation can be up to 40.7% if the magnesium alloy billet is cold-rolled directly. For the cold-rolled Mg alloy plate after annealing at 350 ℃ for 30 - 60 min, the equiaxed fine grain structure with average grain size 9 - 10μm is available.
出处
《东北大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2009年第6期825-828,共4页
Journal of Northeastern University(Natural Science)
基金
国家重点基础研究发展计划项目(2006CB605208-1)
教育部高等学校博士学科点专项科研基金资助项目(20050145021)
关键词
双辊铸轧
AZ31镁合金
显微组织
冷轧
平均晶粒直径
twin-roll casting
AZ31 magnesium alloy
microstructure
cold rolling
average grain size