摘要
Eu2＋ and （or） Eu3＋ doped Sr2SiO4 phosphors particles were synthesized by a conventional solid-state reaction technique, and their structural and optical properties were investigated. The X-ray diffraction （XRD） results showed that the obtained phosphors were composed of orthorhombic α′-Sr2SiO4 and monoclinic β-Sr2SiO4 phase. When excited under 256 nm, Sr2SiO4：Eu3＋ phosphors showed intense emission in the red region. Sr2SiO4：Eu3＋ phosphors exhibited white emissions （x=0.30, y=0.40, Tc=6500 K） ranging from 425 to 650 nm when it was excited by near-ultraviolet （near-UV） light, indicating that Sr2SiOn：Eu2＋ was a good light-conversion phosphor candidate for near-UV chip.
Eu2＋ and （or） Eu3＋ doped Sr2SiO4 phosphors particles were synthesized by a conventional solid-state reaction technique, and their structural and optical properties were investigated. The X-ray diffraction （XRD） results showed that the obtained phosphors were composed of orthorhombic α′-Sr2SiO4 and monoclinic β-Sr2SiO4 phase. When excited under 256 nm, Sr2SiO4：Eu3＋ phosphors showed intense emission in the red region. Sr2SiO4：Eu3＋ phosphors exhibited white emissions （x=0.30, y=0.40, Tc=6500 K） ranging from 425 to 650 nm when it was excited by near-ultraviolet （near-UV） light, indicating that Sr2SiOn：Eu2＋ was a good light-conversion phosphor candidate for near-UV chip.
基金
supported by the grants from the Natural Science Foundation of Zhejiang Province (Y406309)
Research Program from Science and Technology Bureau of Jinhua City (2008-1-151)