摘要
研究了剑麻纤维(SF)的预处理方法、长度和含量对剑麻纤维/聚丙烯(SF/PP)复合材料物理力学性能的影响,采用扫描电子显微镜(SEM)对复合材料的冲击断面进行微观结构分析。实验结果表明:SF经过碱处理和蒸汽爆破处理后,复合材料的冲击强度分别提高了70%、76%;当SF的长度为5￣8mm、含量为20%时复合材料的冲击强度达到最大为21.99kJ/m2;SF含量为50%时弯曲强度、弯曲弹性模量与纯PP相比提高了27.5%、41.1%;熔体流动速率和吸水率随SF含量的增加变化明显。
Effects of modification of sisal fiber （SF）, length and content of SF on physical and mechanical properties of sisal fiber-polypropylene （SF/PP） composites were studied. And the microstructures of impact fracture surface were also analyzed by SEM. The results showed that impact strength of composites treated by alkali and steam explosion ncreased 70% and 76% respectively; when the length of SF was 5～8 mm and the SF content was 20%, the impact strength was best and reached 21.99 k J/m^2; when the content of SF was 50%, bending strength and bending modulus ncreased 27.5% and 41.1 % compared with the pure PP; also, as the content of SF was increased, the melt flow rate and water absorption rate changed noticeably.
出处
《中国人造板》
2009年第1期13-17,共5页
China Wood-Based Panels
基金
国家自然科学基金(50763001)
国家973计划前期研究专项(2008CB617513)
广西优秀人才资助计划(桂教人才0817)
广西教育厅研究生科研创新基金(2007105960805M21)
关键词
剑麻纤维
聚丙烯
复合材料
物理力学性能
sisal fiber
polypropylene
composite
physical and mechanical properties