摘要
For 18 months, a newly developed low alloy weathering steel has been exposed in two coastal sites （Qingdao in the north China, Wanning in the south China）. The different corrosion behaviors of the exposed side and the underside of the samples were characterized by X-ray diffraetion （XRD）, polarization curve, electrochemical impedance spectroscopy （EIS）, scanning electron microscopy （SEM）, and N2 adsorption approach. It was found that the samples exhibited higher corrosion rate in Wanning than that in Qingdao. The underside of the samples corrodes more seriously than the exposed side in Qingdao, whereas the result in Wanning is just the reverse. The protection performance of rust layers mainly depends on its compactness and the enrichment of Cu and Cr is a secondary causation. The different compactness of rust layers in the exposed side and the underside originates from different corrosion conditions of the two sides.
For 18 months, a newly developed low alloy weathering steel has been exposed in two coastal sites （Qingdao in the north China, Wanning in the south China）. The different corrosion behaviors of the exposed side and the underside of the samples were characterized by X-ray diffraetion （XRD）, polarization curve, electrochemical impedance spectroscopy （EIS）, scanning electron microscopy （SEM）, and N2 adsorption approach. It was found that the samples exhibited higher corrosion rate in Wanning than that in Qingdao. The underside of the samples corrodes more seriously than the exposed side in Qingdao, whereas the result in Wanning is just the reverse. The protection performance of rust layers mainly depends on its compactness and the enrichment of Cu and Cr is a secondary causation. The different compactness of rust layers in the exposed side and the underside originates from different corrosion conditions of the two sides.
基金
supported by National Key Basic Research and Development Programof China (No.2004CB619102).