Nd10.5Pr2.5Fe80Nb1B6非晶快淬薄带等温晶化行为及矫顽力研究 被引量:3

Isothermal Crystallization Behaviors and Coercivity of Nd_(10.5)Pr_(2.5)Fe_(80)Nb_1B_6 Amorphous Melt-Spun Ribbons
下载PDF
导出
摘要 研究了Nd10.5Pr2.5Fe80Nb1B6非晶快淬薄带在943,973和1003 K等温晶化与薄带组织和矫顽力的关系。结果表明,Nd10.5Pr2.5Fe80Nb1B6快淬薄带在943 K等温晶化所需晶化孕育时间为12 min,973 K时为5 min,而1003 K时不足5 min。Nd10.5Pr2.5Fe75NbB6在1003 K晶化25 min后所得的(Nd,Pr)2Fe14B平均晶粒尺寸为163 nm,添加Nb显著延缓了Nd10.5Pr2.5Fe80Nb1B6快淬薄带晶化后的晶粒尺寸长大。加Nb,Pr能有效提高Nd10.5Pr2.5Fe80Nb1B6的矫顽力。在973 K晶化处理19 min时得到平均晶粒尺寸为96 nm的(Nd,Pr)2Fe14B单相组织,其最大矫顽力为1616 kA.m-1。 The relationship between microstructures and coercivities of Nd10.5Pr2. 5Fe80NbB6 meh-spun ribbons, after isothermal crystallization processes at 943, 973 and 1003 K, was studied. The results showed that the crystallization in cubation duration was 12, 5 and less than 5 min at 943, 973 and The average grain size of (Nd, 1003 K respectively. Pr)2Fe14B was 163nm, 'after at 1003 K for 25 min, growth of (Nd, Pr)2Fe14B grains. Nb and Pr increased the intrinsic magnets. The best coercive force, obtained after crystallizing at 973 its average grain size was 96 nm. for Nb retarded the The combination of coercive force of the 1616 kA·m^-1, was K for 19 min, and
出处 《中国稀土学报》 CAS CSCD 北大核心 2008年第5期652-655,共4页 Journal of the Chinese Society of Rare Earths
基金 国家重大基础研究前期专项(2004CCA04000) 国家自然科学基金(50744014) 浙江省科技计划重点项目(2008C21046) 浙江省自然科学基金(Y406389) 江西省主要学科跨世纪学术和技术带头人培养计划资助项目(CA99110901) 宁波市科技攻关项目(2006B100054) 宁波大学王宽诚幸福基金
关键词 ND-FE-B 快淬薄带 等温晶化 矫顽力 稀土 Nd-Fe-B melt-spun ribbon isothermal crystallization coercivity rare earths
  • 相关文献

参考文献13

  • 1Ahmad I, Davies H A, Buckley R A. The effect of Nd content on the structure and properties of melt spun Nd-rich Nd-Fe-B alloys [J]. Journal of Magnetism and Magnetic Materials, 1996, 157/158: 31. 被引量:1
  • 2Sun Wensheng, Li Shandong, Quart Mingxiu. The effect of phase constituent on the magnetic properties for melt-spun Ndl5 Fe77Bs ribbons [J]. Journal of Magnetism and Magnetic Materials, 1997, 176: 307. 被引量:1
  • 3Zhang Wenyong, Zhang Shaoying, Yah Aru, Zhang Hongwei, Shen Baogen. Effect of the substitution of Pr for Nd on microstructure and magnetic properties of nanocomposite Nd2Fe14 B/α- Fe magnets [J]. Journal of Magnetism and Magnetic Materials, 2001, 225: 389. 被引量:1
  • 4Betaneourt R J I, Davies H A. Coercivity mechanism in nanophase (Nd-Pr)-Fe-B meh spun alloys [J]. Physica B, 2002, 320: 294. 被引量:1
  • 5Kim Y B, Kim M J, Jin Hanniin, et al. Spin reorientation and magnetocrystalline anisotropy of (Nd1-xPrx)2Fe14B[J ]. Journal of Magnetism and Magnetic Materials, 1999, 191 : 133. 被引量:1
  • 6Zhou Shaoxiong. Johansson P. Savage S J, Cui Liya. Effect of Ga, Si and Nb additions on the phases and magnetic properties of melt-spun Nd-Fe-B allo'.s [J i. IEEE Trans. Magn. MAG, 1990. 26: 1739. 被引量:1
  • 7Kim Y B, Lee K W, Kim C S. Shin H C, Kim T K. Okada M, Honmm M. Nh-added high-coercivity M-Fe-5 melt-spun ribbon with high remanence [J]. J. Appl. Phys.. 1991. 70: 6478. 被引量:1
  • 8Betancourt I, Davies H A. Influence of Zr and Nb dopant additions on tile mierostrueture and magnetic properties of nanocomposite RE2(Fe, Co)14B/α(Fe, Co) (RE= Nd-Pr) alloys [J ].Journal of Magnetism and Magnetic Materials, 2003, 261 : 328. 被引量:1
  • 9Herbst J F. Fuerst C D. Mishra R K, Murphy C B, Van Wingerden D J. Coercivity enhancement of melt-spun Nd-Fe-B ribbons using low-level Cu additions [J]. J. Appl. Phys., 1991, 69: 5823. 被引量:1
  • 10Tkatch V I, Rassolov S G, Moiseeva T N, Popov V V. Analytical description of isothermal primary crystallization kinetics of glasses: Fe85B15 amorphous alloy [J]. Non-Cryst. Solids, 2005, 351: 1658. 被引量:1

同被引文献61

引证文献3

二级引证文献4

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部