The monomer 2,6,12-triaminotriptycene was synthesized and the structure was confirmed by IR and 1H NMR spectra. Hyperbranched polyimides modified with different terminal groups were obtained from precursors, anhydride- and aminoterminated hyperbranched poly（amic acid）s from polymerization of A2 ＋ B3 system. From gel permeation chromatograrn （GPC） characterization, representative products had high molecular weight. All polymers had good solubility in CHCl3, DMF and tetrahydrofuran （THF）, and performed no detective Tgs in the range of 50-300 ℃ and high Tds above 455 ℃ when 5% weight loss.
The monomer 2,6,12-triaminotriptycene was synthesized and the structure was confirmed by IR and 1H NMR spectra. Hyperbranched polyimides modified with different terminal groups were obtained from precursors, anhydride- and aminoterminated hyperbranched poly（amic acid）s from polymerization of A2 ＋ B3 system. From gel permeation chromatograrn （GPC） characterization, representative products had high molecular weight. All polymers had good solubility in CHCl3, DMF and tetrahydrofuran （THF）, and performed no detective Tgs in the range of 50-300 ℃ and high Tds above 455 ℃ when 5% weight loss.
基金
the National Natural Science Foundation(No.50673031)of China and authors would like to extend thanks to Professor Yongming Chen at CAS.