摘要
合成了一系列基于4,4-′ODPA,3,4-′ODPA以及3,3-′ODPA 3种异构二苯醚二酐单体的异构聚酰亚胺,以苯酐(PA)作为封端剂来控制分子量.用DSC和WAXD为主要手段研究了这几种异构聚酰亚胺的结晶行为.研究发现聚酰亚胺4,4-′ODPA/ODA(二苯醚二胺)在分子量较低的情况下能够在热处理,退火或剪切作用下结晶.并且升高热处理温度和延长热处理时间有利于结晶的完善,在玻璃化温度以上施加剪切能够加速聚酰亚胺的结晶.而对于其他的两种异构体3,4-′ODPA/ODA以及3,3-′ODPA/ODA无论是经过热处理还是施加外力剪切都未能使其结晶.
The isomeric effects of dianhydride on the crystalline properties of polyimide were reported, it was acontinuation of isomeric polyimides studies in our group. A series of molecular-weight-controlled isomeric polyimides powders based on three dianhydride isomers, 3,3＇, 4,4＇-oxydiphthalic dianhydride （4,4＇-ODPA）, 2,3＇, 3,4＇- oxydiphthalic dianhydride （3,4＇-ODPA） and 2, 2＇, 3,3＇-oxydiphthalic dianhydride （3,3＇-ODPA）, and 4, 4＇- oxydianiline （ODA） were prepared by traditional two-step method in DMAc, and phthalic anhydride （PA） was usedas end-capper. Wide-angle X-ray diffraction （WAXD） and differential scanning calorimetry （DSC） were used to investigate the crystallization behavior of isomeric polyimides. The annealing temperature, annealing time, external force shearing and molecular weight effects on the crystallization of isomeric polyimides were studied. The results proved that 4,4＇-ODPA/ODA-based polyimide powder was amorphous at room temperature and could crystallize during annealing or shearing process above T~. The crystallization of 4,4＇-ODPA/ODA-based polyimide wasenhanced by increasing the annealing temperature and time, decreasing molecular weight or pushing shearing above Tg. Two melting endo-peaks appeared evidently when the annealing temperature was below 300℃. The two melting peaks tended to be close to each other with the increase of annealing temperature, and only one melting peak was found when annealing temperature reached 370℃. The higher melting temperature of 4,4＇-ODPA/ODA-based polyimide was aroud 370- 380℃,however, this polyimide was difficult to recrystallize once melted. This polyimide was annealed at 370℃ for different times, the amorphous as-prepared samples had crystallized after annealing at 370℃ only in 1 min, besides the crystallinity was increased with the increase of the annealing time, but no crystalline form change was found. The polyimide with low molecular weight was easy to crystallize. It can be seen that the pol
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2008年第3期251-258,共8页
Acta Polymerica Sinica
基金
国家自然科学基金(基金号50333030)
国家重点基础研究发展计划(973计划,项目号G2003CB615604和2003CB615704)资助项目
关键词
聚酰亚胺
结晶
异构二酐
异构体
Polyimides, Crystallization, Isomeric dianhydride, Isomers