摘要
This work intends to investigate the inhibition behaviour of 2-butine 1, 4diol and potassium sodium tartrate and their synergistic effects on 3003 aluminium alloy corrosion in 0.5% NaCl solution. Experiments were carried out by electrochemical impedance spectroscopy （EIS） and Tafel polarization method in a three-electrode cell. It was concluded that the inhibition efficiencies increased with an increase in the concentrations of inhibitors. For 2-butinel, 4diol and tartrate salt, the optimum in the inhibition efficiency, at room temperature and neutral pH, was observed for concentrations close to 10-3 mol/L and 1.5×10^-3mol/L, respectively. The electrochemical results illustrated that 2-butinel, 4diol and tartrate salt, have significant synergistic inhibition effects on corrosion of 3003 aluminium alloy in 0.5% NaCl solution. The optimum ratio of concentrations for tartrate to alcohol was 2：1.
This work intends to investigate the inhibition behaviour of 2-butine 1, 4diol and potassium sodium tartrate and their synergistic effects on 3003 aluminium alloy corrosion in 0.5% NaCl solution. Experiments were carried out by electrochemical impedance spectroscopy （EIS） and Tafel polarization method in a three-electrode cell. It was concluded that the inhibition efficiencies increased with an increase in the concentrations of inhibitors. For 2-butinel, 4diol and tartrate salt, the optimum in the inhibition efficiency, at room temperature and neutral pH, was observed for concentrations close to 10-3 mol/L and 1.5×10^-3mol/L, respectively. The electrochemical results illustrated that 2-butinel, 4diol and tartrate salt, have significant synergistic inhibition effects on corrosion of 3003 aluminium alloy in 0.5% NaCl solution. The optimum ratio of concentrations for tartrate to alcohol was 2：1.