The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.
The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.
基金
Project supported by the Hebei Provincial Technology Development Foundation (51215103b)
Science Foundation of Hebei University (2006Q06)