透极远红外光学材料制备及性能研究

Study on preparation and performance of extra-far infrared optical material
原文传递
导出
摘要 在一定的温度、压力等条件下,采用有机材料(聚四氟乙烯)和无机晶体(KBr、CsI),通过热合技术研制出样品几何尺寸为Φ20mm×3-5mm、透射波段分别为15-38μm(PE-KBr)和15-60μm(PE-CsI)的透极远红外复合光学材料。抗腐蚀性能测试结果表明,材料耐强酸、强碱及部分有机溶剂。机械性能分析表明材料在小于115℃范围内可安全使用。极远红外透过率测试结果表明,在1-15μm波段,平均透过率小于15%,15-38μm和15-60μm极远红外波段,平均透过率大于50%,并对影响材料透过率的因素进行了分析。 The inorganic crystal material KBr and teflon as organic protective material is used as 15-38μm,15-60μm wide-waveband extra-far infrared window material by thermal synthesis technology.The sample size is Φ20mm×3-5mm.The result of anti-corrodent indicated that the material can endure strong acid,strong alkali and part of organic solvent.The material can be used under 115 centigrade according to the mechanical intensation analysis.The result of infrared transimissivity test indicates that its transimissivity is above 50% in 15-38μm and 15-60μm waveband and below 15% in 1-15μm waveband.The influence factor of material transmittance is analysized.
出处 《光学技术》 CAS CSCD 北大核心 2008年第1期68-70,74,共4页 Optical Technique
基金 总装备部项目(41312040102)
关键词 极远红外 热合技术 有机-无机复合红外光学材料 extra-far infrared thermal synthesis technology organic-inorganic synthetic infrared optical material
  • 相关文献

参考文献4

  • 1Guiderdoni B, Bouchet F R, Derrient J. The Fir/Submm Window on Galaxy Formation[J]. Kluwer Academic Publishers,2003,1: 1--10. 被引量:1
  • 2Maiwald F, et al. Microware Theory and Techniques society International symposium Digest . IEEE, 2001,3:1637--1640. 被引量:1
  • 3曹莹,李建利,孙晶,于薇,曾繁明,万玉春.15-50μm宽波段远红外窗口材料的研制[J].长春理工大学学报(自然科学版),2004,27(4):27-29. 被引量:4
  • 4Gustin E,Wenseleers W, Leblans M, et al. Influence of OH-impurities on the relaxation of F centers studied with picosecond optical pulse[J]. Radiat.Eff. Defects Solids, 1995,134:498--492. 被引量:1

二级参考文献4

共引文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部