摘要
A 2D woven graphite fibers reinforced aluminum matrix composite with 50%Grf (volume fraction) was fabricated by the squeeze-casting technology, and its microstructure and mechanical properties were investigated. The results show that the composite is dense, the graphite fibers are distributed uniformly in the composite. TEM observation indicates the bonding between fiber and matrix is good and little interfacial reaction is found in the Grf/Al composite. This is attributed to the better stability of graphite fiber and the fabrication process minimizing the contact time between fiber with matrix at high temperatures. The 2D woven Grf/Al composite exhibites better mechanical properties with tensile strength, bending strength and elastic modulus of 366.2, 519.7 and 110.7 GPa, respectively. SEM images suggeste that the fracture is irregular and some pulled-out fibers are found, which indicats that the high strength of fiber is not degraded.
A 2D woven graphite fibers reinforced aluminum matrix composite with 50%Grf （volume fraction） was fabricated by the squeeze-casting technology, and its microstructure and mechanical properties were investigated. The results show that the composite is dense, the graphite fibers are distributed uniformly in the composite. TEM observation indicates the bonding between fiber and matrix is good and little interfacial reaction is found in the Grf/Al composite. This is attributed to the better stability of graphite fiber and the fabrication process minimizing the contact time between fiber with matrix at high temperatures. The 2D woven Grf/Al composite exhibites better mechanical properties with tensile strength, bending strength and elastic modulus of 366.2, 519.7 and 110.7 GPa, respectively.＂ SEM images suggeste that the fracture is irregular and some pulled-out fibers are found, which indicats that the high strength of fiber is not degraded.
出处
《中国有色金属学会会刊：英文版》
CSCD
2006年第A03期1509-1512,共4页
Transactions of Nonferrous Metals Society of China
关键词
铝合金
金属化合物
机械性能
石墨
纤维
2D woven composites
graphite fiber
aluminum matrix composites
mechanical property