摘要
A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclodextrin template had the higher surface areas （124-484 m^2/g）, larger pore volumes （0.7-1.27 mL/g） and more thermal stability than samples prepared without using β-cyclodextrin.
A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclodextrin template had the higher surface areas （124-484 m^2/g）, larger pore volumes （0.7-1.27 mL/g） and more thermal stability than samples prepared without using β-cyclodextrin.