摘要
用６５份黑索今（０．６５份高聚物包覆的）和３５份梯恩梯进行真空熔药（温度８５～９０℃），然后注入模具中，在室温下降温，凝固制成梯黑药柱。用渗油性和尺寸测量的方法测得结果表明：该药柱的渗油性和不可逆长大量，均明显地低于含ＭＮＴ的梯黑（ＲＨＴ－９０２）药柱。
parts of RDX crystal coated with 0.65 part of polymer and 35 parts ofTNT were mixed and molten under vacuum at 85～90℃,then cast into aluminummoulds and let them solidify at room temperature,The results of exudation test and di-mension of charges measured show that the exudate weights, irreversible growth valuesand density decrements of said charges are much less than those of RDX/TNT/MNT64. 78/34. 88/0. 34(wt%)charges,where MNT is m- and p-mononitrotoluene.
出处
《含能材料》
EI
CAS
CSCD
1994年第1期7-11,共5页
Chinese Journal of Energetic Materials
关键词
梯黑药柱
渗油性
不可逆长大
改性
药柱
cast RDX-TNT charges,exudating test,irreversible growth.