摘要
本文通过对现场腐蚀产物表面分析、采用失重法、极化曲线的测定研究了S135钢在磺化钻井液中的腐蚀行为,结果表明:氧是引起腐蚀的主要原因。并通过XPS分析对腐蚀机理进行了探讨。
Corrosion behavior of S135 steel in sulphonated drilling fluids was studied by the corrosion production analysis, means of weight loss and polarization curves ,The experiment results revealed that the existing of dissolved oxygen is the main factor to corrosion. And corrosion mechanism was also explored by XPS analysis in the paper.
出处
《全面腐蚀控制》
2005年第2期29-31,34,共4页
Total Corrosion Control