摘要
用Al-Zn-Si合金粉末制备热烧结铝锌硅合金涂层,通过盐水浸泡实验和电化学测试研究其耐蚀性能,并结合扫描电镜和X射线衍射分析等手段观察A1-Zn-Si合金涂层显微组织及其在盐水中的腐蚀产物形貌,分析涂层的耐蚀机理。结果表明,Al-Zn-Si合金涂层也具有阴极保护作用,且Al-Zn-Si合金延缓涂层金属粉末的消耗,使牺牲阳极的腐蚀速率减慢。
A kind of anti-corrosive paint consisted of epoxy silane and lamellar Al-Zn-Si alloy particles was introduced in this paper. Corrosion properties of waterborne Al-Zn-Si alloy coating were tested through salt water immersion method, electrochemical method. Furthermore, the microstructure, corrosion products of the coating were detected by means of SEM, EDS and XRD. The experimental results showed that Al-Zn-Si alloy particles dispersed in coating in the form of flake structure which formed a more effective physical shield, extending the path of the corrosive medium to body; furthermore, in the corrosion processes corrosion product film formed which filled in pores of the coating and had good shielding property; Tafel curves indicated that Al-Zn-Si alloy was a good sacrificial anode material of aluminum. In addition, anti-corrosive mechanism of Al-Zn-Si alloy coating was analyzed which possessed excellent cathodic protection, and its excellent corrosion resistance was related to lamellar AI-Zn-Si alloy powder which had lower dissolution rate, inhibited the corrosion of the coating and prolonged the duration of cathodic protection.
出处
《中国腐蚀与防护学报》
CAS
CSCD
北大核心
2012年第4期311-316,共6页
Journal of Chinese Society For Corrosion and Protection
基金
江苏省普通高校研究生科研创新计划项目(CXLX120149)
江苏省科技成果转化专项基金(BA2011029)
江苏省产学研联合创新资金-前瞻性联合研究项目(BY2011101)
江苏省普通高校研究生科研创新计划资助项目(CXLX12-0149)
中央高校基本科研业务费专项资金资助
关键词
Al-Zn-Si合金涂层
防腐涂料
盐水腐蚀
阴极保护
Al-Zn-Si alloy coating, corrosion protective coatings, salt water corrosion, cathodic protection