摘要
This paper presents the effects of aging processes on the properties and microstructure of Cu-0.3Cr-0.15Zr-0.05Mg lead frame alloy. Optimal conditions for good hardening and electrical conductivity can be obtained by solution treating at 920 °C for Ih and aging at 470^0 for 4h and at 550^ for Ih. The hardness and electrical conductivity can reach 108HV, 73%IACS and 106HV, 76%IACS, respectively. Aging precipitation was dealt with by transmission electronic microscope (TEM). At 470 °C aging for 4h the fine precipitation of an ordered compound CrCu2(Zr,Mg) is found in matrix as well as fine Cr and Cu4Zr. Aging at 550’C for Ih some precipitates are still coherent with matrix. The CrCu2(Zr,Mg) completely dissolves into Cr and Cu4Zr.
This paper presents the effects of aging processes on the properties and microstructure of Cu-0.3Cr-0.15Zr-0.05Mg lead frame alloy. Optimal conditions for good hardening and electrical conductivity can be obtained by solution treating at 920 °C for Ih and aging at 470^0 for 4h and at 550^ for Ih. The hardness and electrical conductivity can reach 108HV, 73%IACS and 106HV, 76%IACS, respectively. Aging precipitation was dealt with by transmission electronic microscope (TEM). At 470 °C aging for 4h the fine precipitation of an ordered compound CrCu2(Zr,Mg) is found in matrix as well as fine Cr and Cu4Zr. Aging at 550'C for Ih some precipitates are still coherent with matrix. The CrCu2(Zr,Mg) completely dissolves into Cr and Cu4Zr.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2004年第5期157-160,共4页
Transactions of Materials and Heat Treatment