摘要
为了改善Fe粉的微波吸收性能,采用sol-gel法与H_2还原法制备了w(Al_2O_3)为0.5%~5.0%的Fe/Al_2O_3复合粉。利用SEM和激光粒度分析仪分析了所制粉末的形貌与粒度分布;并将所制复合粉末与石蜡按质量比80:20制成Fe/Al_2O_3/石蜡复合材料,研究w(Al_2O_3)对复合材料微波吸收性能的影响。结果表明:Fe/Al_2O_3复合粉的外形呈片状与针状,其粒度分布很宽。当w(Al_2O_3)由0增加到5.0%时,复合材料的复介电常数实部ε′从11增加至21;复磁导率虚部μ″呈多模共振的曲线形式;w(Al_2O_3)为2.0%,厚为2mm的Fe/Al_2O_3/石蜡复合材料的–5dB反射损失R频宽为4.6GHz。
To improve the microwave absorbing property of Fe powder, Fe/Al2O3 compound powder containing 0.5%~5.0% (mass fraction) of Al2O3 was prepared by the sol-gel method and H2 reduction method, respectively. The morphology and particle size distribution of the prepared powder were characterized with SEM and laser particle size analyzer. The Fe/Al2O3/wax composite materials were fabricated from prepared Fe/Al2O3 compound powder and wax at a mass ratio of 80:20. The effect of w(Al2O3) doped on the microwave absorb...
出处
《电子元件与材料》
CAS
CSCD
北大核心
2010年第7期4-7,共4页
Electronic Components And Materials
基金
国家自然科学基金资助项目(No.20971027)
高等学校博士学科点专项科研基金资助项目(No.20094420110005)
广东省自然科学基金资助项目(No.07001769
No.9251009001000006)
广东省科技计划资助项目(No.2009A030301008
No.2009B090300017)
粤港关键领域重点突破招标项目(No.20071683)
东南大学毫米波国家重点实验室开放课题(No.K200921)
广州市科技计划资助项目(No.2009J1-C381)