MnO_2/activated carbon composite（Mn-ACC） wave absorber was prepared by the reaction between Mn（CH_3COO）_2 and KMnO_4 on activated carbon. Then, a novel cement based composite absorbing coating（CB-CAC） was prepar...MnO_2/activated carbon composite（Mn-ACC） wave absorber was prepared by the reaction between Mn（CH_3COO）_2 and KMnO_4 on activated carbon. Then, a novel cement based composite absorbing coating（CB-CAC） was prepared by adding the Mn-ACC, manganese zinc ferrite and rubber particles into cement. XRD method was used to analyze the reaction products of the Mn-ACC. The tensile bond strength and the wave absorbing properties of the CB-CACs were also tested. The results showed that the crystallinity of MnO_2 formed in the Mn-ACC was poor. Adding Mn-ACC into the CB-CAC led to first increase and then decrease of the tensile bond strength. The tensile bond strength reached 1.89 MPa with 8.51% of the Mn-ACC. The CB-CACs obtained the optimal absorbing properties with the cement, manganese zinc ferrite, Mn-ACC, rubber particles and H_2O mass ratio of 7.5？7.5？1？1？5.5, respectively. The band width of the reflection below-10 dB was up to 8.8 GHz, which accounted for 57.14% of the test band.展开更多
基金Funded by the International Cooperation Office of the Ministry of Science and Technology of China(2013DFR50360)the Postdoctoral Research Foundation of Shenyang Ligong University,the Open Fund from Advanced Processing Technology of Metal Materials of Liaoning Key Laboratory,Shenyang Ligong Universitythe Guide Project from Liaoning Natural Science Foundation of China(No.201602646)
文摘MnO_2/activated carbon composite（Mn-ACC） wave absorber was prepared by the reaction between Mn（CH_3COO）_2 and KMnO_4 on activated carbon. Then, a novel cement based composite absorbing coating（CB-CAC） was prepared by adding the Mn-ACC, manganese zinc ferrite and rubber particles into cement. XRD method was used to analyze the reaction products of the Mn-ACC. The tensile bond strength and the wave absorbing properties of the CB-CACs were also tested. The results showed that the crystallinity of MnO_2 formed in the Mn-ACC was poor. Adding Mn-ACC into the CB-CAC led to first increase and then decrease of the tensile bond strength. The tensile bond strength reached 1.89 MPa with 8.51% of the Mn-ACC. The CB-CACs obtained the optimal absorbing properties with the cement, manganese zinc ferrite, Mn-ACC, rubber particles and H_2O mass ratio of 7.5？7.5？1？1？5.5, respectively. The band width of the reflection below-10 dB was up to 8.8 GHz, which accounted for 57.14% of the test band.