In this study, Al_2O_3-washcoated SiC(Al_2O_3–SiC) foams and Al_2O_3 powder were employed as the supports of a Ni catalyst for the liquid-phase hydrogenation of benzaldehyde. A series of Ni/Al_2O_3–SiC foam catalyst...In this study, Al_2O_3-washcoated SiC(Al_2O_3–SiC) foams and Al_2O_3 powder were employed as the supports of a Ni catalyst for the liquid-phase hydrogenation of benzaldehyde. A series of Ni/Al_2O_3–SiC foam catalysts and Ni/Al_2O_3 powder catalysts with a Ni loading from 10 wt% to 37 wt% of the weight of Al_2O_3 were first prepared by a deposition–precipitation(DP) method. The catalytic activity and recyclability of both kinds of catalysts were then compared. Although it had a smaller accessible surface area with the reactant, the foam catalyst with a Ni loading of 16 wt% exhibited a slightly higher conversion of benzaldehyde after 6 h(of 99.3%) in comparison with the Ni/Al_2O_3 catalyst with identical Ni loading(conversion of 97.5%). When the Ni loading increased from 16 wt% to 37 wt%, the reaction rate obtained with the foam catalyst increased significantly from 0.108 to 0.204 mol L^(-1)h^(-1), whereas the reaction rate obtained with the powder catalyst increased from 0.106 to 0.123 mol L^(-1)h^(-1). Furthermore, the specific activity(moles of benzaldehyde consumed by 1 g min^(-1)of Ni) of the foam catalyst with a Ni loading above 30 wt% was superior to that of the powder catalyst because of its smaller Ni-particle size and higher mass-transfer rate. The foam catalyst displayed a high recyclability as a function of run times owing to the strong interaction between the Ni component and the Al_2O_3 coating. The conversion of benzaldehyde over the foam catalyst remained almost unchanged after being used 8 times. In comparison, a drop of 43% in the conversion of benzaldehyde with the powder catalyst was observed after being used 7 times due to the leaching of the Ni component.展开更多
基金the financial support of the project from the National Key Research&Development Program of China(No.2017YFB0310405)
文摘In this study, Al_2O_3-washcoated SiC(Al_2O_3–SiC) foams and Al_2O_3 powder were employed as the supports of a Ni catalyst for the liquid-phase hydrogenation of benzaldehyde. A series of Ni/Al_2O_3–SiC foam catalysts and Ni/Al_2O_3 powder catalysts with a Ni loading from 10 wt% to 37 wt% of the weight of Al_2O_3 were first prepared by a deposition–precipitation(DP) method. The catalytic activity and recyclability of both kinds of catalysts were then compared. Although it had a smaller accessible surface area with the reactant, the foam catalyst with a Ni loading of 16 wt% exhibited a slightly higher conversion of benzaldehyde after 6 h(of 99.3%) in comparison with the Ni/Al_2O_3 catalyst with identical Ni loading(conversion of 97.5%). When the Ni loading increased from 16 wt% to 37 wt%, the reaction rate obtained with the foam catalyst increased significantly from 0.108 to 0.204 mol L^(-1)h^(-1), whereas the reaction rate obtained with the powder catalyst increased from 0.106 to 0.123 mol L^(-1)h^(-1). Furthermore, the specific activity(moles of benzaldehyde consumed by 1 g min^(-1)of Ni) of the foam catalyst with a Ni loading above 30 wt% was superior to that of the powder catalyst because of its smaller Ni-particle size and higher mass-transfer rate. The foam catalyst displayed a high recyclability as a function of run times owing to the strong interaction between the Ni component and the Al_2O_3 coating. The conversion of benzaldehyde over the foam catalyst remained almost unchanged after being used 8 times. In comparison, a drop of 43% in the conversion of benzaldehyde with the powder catalyst was observed after being used 7 times due to the leaching of the Ni component.
