The ionic conductivity (at room temperature) of nano-LaF3 bulk material and a new discovered phenomenon of increasing ionic conductivity caused by grain boundary relaxation activated by AC (alternating current) shocki...The ionic conductivity (at room temperature) of nano-LaF3 bulk material and a new discovered phenomenon of increasing ionic conductivity caused by grain boundary relaxation activated by AC (alternating current) shocking were reported. Nano-crystalline powder of LaF3 with average grain size of 16.7 nm was synthesized with a method of direct precipitation from aqueous solution. Particle size and shape of LaF3 nano-crystalline powder were analyzed by XRD and TEM. Nano-LaF3 bulk material was prepared by compacting the powder to 1 GPa at room temperature and vacuum of 10?4 Pa. The ionic conductivity of nano-LaF3 bulk material was studied with complex impedance spectra at room temperature. The ionic conductivity of nano-LaF3 bulk material (10?5 S/cm) at room temperature is significantly increased compared with that of single crystal LaF3 (10?6 S/cm). A special phenomenon is observed for the first time that the ionic conductivity increases gradually with AC scanning times.展开更多
Nanocrystalline powder of LaF3 was synthesized by a method of direct precipitation from water solution. Particle size and shape of LaF3 nanocrystalline powder was analysed with TEM. Particles were mainly spherical wit...Nanocrystalline powder of LaF3 was synthesized by a method of direct precipitation from water solution. Particle size and shape of LaF3 nanocrystalline powder was analysed with TEM. Particles were mainly spherical with narrow particle size distribution （10 20 nm）. The average particle size analysed with XRD is 16.7 nm. Nano-LaF3 bulk material was prepared by compacting the powder to 1 GPa at room temperature and a vacuum of 10^-4 Pa. The ionic conductivity of nano-LaF3 bulk material was studied with complex impedance spectra at room temperature. The ionic conductivity of nano-LaF3 bulk material （1 × 10^-5 S·cm^-1 ） at room temperature is significantly increased compared to that of single crystal LaF3 （1 × 10^-6 S·cm^-1）. A special phenomenon was observed firstly time that the ionic conductivity increased gradually with multiple testing in result of relaxation.展开更多
基金Project(59872031) supported by the National Natural Science Foundation of China
文摘The ionic conductivity (at room temperature) of nano-LaF3 bulk material and a new discovered phenomenon of increasing ionic conductivity caused by grain boundary relaxation activated by AC (alternating current) shocking were reported. Nano-crystalline powder of LaF3 with average grain size of 16.7 nm was synthesized with a method of direct precipitation from aqueous solution. Particle size and shape of LaF3 nano-crystalline powder were analyzed by XRD and TEM. Nano-LaF3 bulk material was prepared by compacting the powder to 1 GPa at room temperature and vacuum of 10?4 Pa. The ionic conductivity of nano-LaF3 bulk material was studied with complex impedance spectra at room temperature. The ionic conductivity of nano-LaF3 bulk material (10?5 S/cm) at room temperature is significantly increased compared with that of single crystal LaF3 (10?6 S/cm). A special phenomenon is observed for the first time that the ionic conductivity increases gradually with AC scanning times.
文摘Nanocrystalline powder of LaF3 was synthesized by a method of direct precipitation from water solution. Particle size and shape of LaF3 nanocrystalline powder was analysed with TEM. Particles were mainly spherical with narrow particle size distribution （10 20 nm）. The average particle size analysed with XRD is 16.7 nm. Nano-LaF3 bulk material was prepared by compacting the powder to 1 GPa at room temperature and a vacuum of 10^-4 Pa. The ionic conductivity of nano-LaF3 bulk material was studied with complex impedance spectra at room temperature. The ionic conductivity of nano-LaF3 bulk material （1 × 10^-5 S·cm^-1 ） at room temperature is significantly increased compared to that of single crystal LaF3 （1 × 10^-6 S·cm^-1）. A special phenomenon was observed firstly time that the ionic conductivity increased gradually with multiple testing in result of relaxation.