The design and sizing of new mechanical components which are intended to operate under cyclic loads often require an acceptable level of confidence that the components will meet pre-defined fatigue strength objectives...The design and sizing of new mechanical components which are intended to operate under cyclic loads often require an acceptable level of confidence that the components will meet pre-defined fatigue strength objectives for crack initiation. For loads with multiple amplitudes and mean values, models based on Palmgren-Miner’s linear cumulative damage hypothesis and on multiple S/N curves (stress-no. cycles) are widely used in estimations for the duration of crack initiation. In this paper a procedure for generating S/N curves for multiple stress ratios by interpolation or extrapolation from the data available for two such curves is proposed. At any number of cycles, the stress for crack initiation is calculated from the far field macroscopic stresses of the known curves using Dang Van fatigue criterion and microscopic stresses evaluated at the grain level. An algorithm is presented for uniaxial loading and results verifications against curves established from laboratory tests with elastic and plastic stresses are shown and discussed for notched and un-notched specimens.展开更多
文摘The design and sizing of new mechanical components which are intended to operate under cyclic loads often require an acceptable level of confidence that the components will meet pre-defined fatigue strength objectives for crack initiation. For loads with multiple amplitudes and mean values, models based on Palmgren-Miner’s linear cumulative damage hypothesis and on multiple S/N curves (stress-no. cycles) are widely used in estimations for the duration of crack initiation. In this paper a procedure for generating S/N curves for multiple stress ratios by interpolation or extrapolation from the data available for two such curves is proposed. At any number of cycles, the stress for crack initiation is calculated from the far field macroscopic stresses of the known curves using Dang Van fatigue criterion and microscopic stresses evaluated at the grain level. An algorithm is presented for uniaxial loading and results verifications against curves established from laboratory tests with elastic and plastic stresses are shown and discussed for notched and un-notched specimens.