To investigate the effects of rotation speed and shearing time on morphology of semisolid AZ91D alloy,experimental work was undertaken using a twin-screw slurry maker.The results show that increasing the rotation spee...To investigate the effects of rotation speed and shearing time on morphology of semisolid AZ91D alloy,experimental work was undertaken using a twin-screw slurry maker.The results show that increasing the rotation speed and reasonable time can give rise to substantial grain refinement during continuous shearing stage,which can be attributed to the increasing of effective nucleation rate caused by the extremely uniform temperature due to high shear rate and high degree of turbulence.Comparing with low rotation speed at the same thermal condition,the analysis indicates that the microstructures obtained at high rotation speed are homogenous spherical and fine grains instead of dendritic or rosette and exhibits uniform distribution in the eutectic matrix.展开更多
高温气冷堆氦气透平直接发电项目中的能量转换单元内使用了联轴器,用来联接氦气透平和齿轮箱。本文在三维设计软件CATIA内建立了联轴器的装配模型,在ABAQUS for CATIA内对联轴器的应力进行了分析计算。计算结果表明,由旋转离心力所引起...高温气冷堆氦气透平直接发电项目中的能量转换单元内使用了联轴器,用来联接氦气透平和齿轮箱。本文在三维设计软件CATIA内建立了联轴器的装配模型,在ABAQUS for CATIA内对联轴器的应力进行了分析计算。计算结果表明,由旋转离心力所引起的最大Von Mises应力为303MPa,由螺栓预紧力引起的最大Von Mises应力为167MPa,由联轴器传递的扭矩引起的应力为1MPa量级,前两个应力最大值发生位置都在最大外径处的螺栓开孔位置,最大应力叠加后为470MPa。由此得出结论,制作联轴器的材料必须是在470MPa的应力水平下不失效的高强度材料。展开更多
基金Project (2009DFB50210) supported by the International Cooperation in Technical Research and Development Program of ChinaProject (2009AA03Z534) supported by the National High-Tech Research and Development Program of ChinaProject (2006CB605203) supported by the National Basic Research Program of China
文摘To investigate the effects of rotation speed and shearing time on morphology of semisolid AZ91D alloy,experimental work was undertaken using a twin-screw slurry maker.The results show that increasing the rotation speed and reasonable time can give rise to substantial grain refinement during continuous shearing stage,which can be attributed to the increasing of effective nucleation rate caused by the extremely uniform temperature due to high shear rate and high degree of turbulence.Comparing with low rotation speed at the same thermal condition,the analysis indicates that the microstructures obtained at high rotation speed are homogenous spherical and fine grains instead of dendritic or rosette and exhibits uniform distribution in the eutectic matrix.
文摘高温气冷堆氦气透平直接发电项目中的能量转换单元内使用了联轴器,用来联接氦气透平和齿轮箱。本文在三维设计软件CATIA内建立了联轴器的装配模型,在ABAQUS for CATIA内对联轴器的应力进行了分析计算。计算结果表明,由旋转离心力所引起的最大Von Mises应力为303MPa,由螺栓预紧力引起的最大Von Mises应力为167MPa,由联轴器传递的扭矩引起的应力为1MPa量级,前两个应力最大值发生位置都在最大外径处的螺栓开孔位置,最大应力叠加后为470MPa。由此得出结论,制作联轴器的材料必须是在470MPa的应力水平下不失效的高强度材料。