The effect of step-quenching on the microstructure of aluminum alloy 7055 after artificial aging was studied by hardness testing and transmission electron microscopy (TEM). Step-quenching leads to decomposition of sol...The effect of step-quenching on the microstructure of aluminum alloy 7055 after artificial aging was studied by hardness testing and transmission electron microscopy (TEM). Step-quenching leads to decomposition of solid solution and heterogeneous precipitation of equilibrium phase mainly on dispersoids and at grain boundaries; thus lower hardness after aging. Prolonging isothermal holding at 415 ℃ results in coarser and more spaced η phase particles at grain boundaries with wider precipitates free zone, and lower density of larger η′ hardening precipitates inside grains after aging. Isothermal holding at 355 ℃ results in heterogeneous precipitation of η phase both on dispersoids and at grain boundaries. Isothermal holding at 235 ℃ results in heterogeneous precipitation of η phase first, and then S phase. Precipitates free zones are created around these coarse η and S phase particles after aging. Prolonging isothermal holding at these two temperatures leads to fewer η′ hardening precipitates inside grains, larger and more spaced η phase particles at grain boundaries and wider grain boundary precipitates free zone after aging.展开更多
The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(...The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(28)Al_(4)Ti_(3)Co_(3) immiscible high-entropy alloy(HEA)was developed.After vacuum arc melting and copper mold suction casting,this HEA exhibits a unique phase separation microstructure,which consists of striped Cu-rich regions and Fe-rich region.Further magnification of the striped Cu-rich region reveals that it is composed of a Cu-rich dot-like phase and a Fe-rich region.The aging alloy is further strengthened by a L1_(2)-Ni_(3)(AlTi)nanoprecipitates,achieving excellent yield strength(1185 MPa)and uniform ductility(~8.8%).The differential distribution of the L1_(2) nanoprecipitate in the striped Cu-rich region and the external Fe-rich region increased the strength difference between these two regions,which increased the strain gradient and thus improved hetero-deformation induced(HDI)hardening.This work provides a new route to improve the HDI hardening of Fe-Cu alloys.展开更多
Precipitation strengthening provides one of the most widely-used mechanisms for strengthen-ing multi-principal-element alloys(MPEAs).Here,we report dual-morphology B2 precipitates in Co_(36)Cr_(15)Fe_(18)Ni_(18)Al_(8)...Precipitation strengthening provides one of the most widely-used mechanisms for strengthen-ing multi-principal-element alloys(MPEAs).Here,we report dual-morphology B2 precipitates in Co_(36)Cr_(15)Fe_(18)Ni_(18)Al_(8)Ti_(4)Mo_(1)MPEA obtained by thermo-mechanical processing.Electron microscopy charac-terization reveals that the dual-morphology B2 precipitates are either recrystallized B2 particles formed at the grain boundaries or triple junctions with recrystallization process,or rod-like within the non-recrystallized FCC matrix.The dual-morphology B2 precipitates enhance the yield strength and ultimate tensile strength up to 1120 MPa and 1480 MPa,respectively.This work suggests the mechanical proper-ties of the alloy can be optimized by B2 precipitation strengthening to meet the needs of engineering applications.展开更多
The quench sensitivity of 6063 alloy was investigated via constructing time-temperature-property（TTP） curves by interrupted quenching technique and transmission electron microscopy（TEM） analysis.The results show t...The quench sensitivity of 6063 alloy was investigated via constructing time-temperature-property（TTP） curves by interrupted quenching technique and transmission electron microscopy（TEM） analysis.The results show that the quench sensitivity of 6063 alloy is lower than that of 6061 or 6082 alloy,and the critical temperature ranges from 300 to 410℃ with the nose temperature of about 360℃.From TEM analysis,heterogeneous precipitate β-Mg2Si is prior to nucleate on the（AlxFeySiz） dispersoids in the critical temperature range,and grows up most rapidly at the nose temperature of 360℃.The heterogeneous precipitation leads to a low concentration of solute,which consequently reduces the amount of the strengthening phase β＇＇ after aging.In the large-scale industrial production of 6063 alloy,the cooling rate during quenching should be enhanced as high as possible in the quenching sensitive temperature range（410-300℃） to suppress the heterogeneous precipitation to get optimal mechanical properties,and it should be slowed down properly from the solution temperature to 410℃ and below 300℃ to reduce the residual stress.展开更多
基金Project(2005CB623706) supported by the National Basic Research Program of China
文摘The effect of step-quenching on the microstructure of aluminum alloy 7055 after artificial aging was studied by hardness testing and transmission electron microscopy (TEM). Step-quenching leads to decomposition of solid solution and heterogeneous precipitation of equilibrium phase mainly on dispersoids and at grain boundaries; thus lower hardness after aging. Prolonging isothermal holding at 415 ℃ results in coarser and more spaced η phase particles at grain boundaries with wider precipitates free zone, and lower density of larger η′ hardening precipitates inside grains after aging. Isothermal holding at 355 ℃ results in heterogeneous precipitation of η phase both on dispersoids and at grain boundaries. Isothermal holding at 235 ℃ results in heterogeneous precipitation of η phase first, and then S phase. Precipitates free zones are created around these coarse η and S phase particles after aging. Prolonging isothermal holding at these two temperatures leads to fewer η′ hardening precipitates inside grains, larger and more spaced η phase particles at grain boundaries and wider grain boundary precipitates free zone after aging.
基金Projects(52001083,52171111,U2141207)supported by the National Natural Science Foundation of ChinaProject(LH2020E060)supported by the Natural Science Foundation of Heilongjiang,China。
文摘The low-cost Fe-Cu,Fe-Ni,and Cu-based high-entropy alloys exhibit a widespread utilization prospect.However,these potential applications have been limited by their low strength.In this study,a novel Fe_(31)Cu_(31)Ni_(28)Al_(4)Ti_(3)Co_(3) immiscible high-entropy alloy(HEA)was developed.After vacuum arc melting and copper mold suction casting,this HEA exhibits a unique phase separation microstructure,which consists of striped Cu-rich regions and Fe-rich region.Further magnification of the striped Cu-rich region reveals that it is composed of a Cu-rich dot-like phase and a Fe-rich region.The aging alloy is further strengthened by a L1_(2)-Ni_(3)(AlTi)nanoprecipitates,achieving excellent yield strength(1185 MPa)and uniform ductility(~8.8%).The differential distribution of the L1_(2) nanoprecipitate in the striped Cu-rich region and the external Fe-rich region increased the strength difference between these two regions,which increased the strain gradient and thus improved hetero-deformation induced(HDI)hardening.This work provides a new route to improve the HDI hardening of Fe-Cu alloys.
基金supported by the Central Guidance on Local Science and Technology Development Fund of Hebei Province(No.216Z1012G)the National Natural Science Foundation of China(No.12174274).
文摘Precipitation strengthening provides one of the most widely-used mechanisms for strengthen-ing multi-principal-element alloys(MPEAs).Here,we report dual-morphology B2 precipitates in Co_(36)Cr_(15)Fe_(18)Ni_(18)Al_(8)Ti_(4)Mo_(1)MPEA obtained by thermo-mechanical processing.Electron microscopy charac-terization reveals that the dual-morphology B2 precipitates are either recrystallized B2 particles formed at the grain boundaries or triple junctions with recrystallization process,or rod-like within the non-recrystallized FCC matrix.The dual-morphology B2 precipitates enhance the yield strength and ultimate tensile strength up to 1120 MPa and 1480 MPa,respectively.This work suggests the mechanical proper-ties of the alloy can be optimized by B2 precipitation strengthening to meet the needs of engineering applications.
文摘The quench sensitivity of 6063 alloy was investigated via constructing time-temperature-property（TTP） curves by interrupted quenching technique and transmission electron microscopy（TEM） analysis.The results show that the quench sensitivity of 6063 alloy is lower than that of 6061 or 6082 alloy,and the critical temperature ranges from 300 to 410℃ with the nose temperature of about 360℃.From TEM analysis,heterogeneous precipitate β-Mg2Si is prior to nucleate on the（AlxFeySiz） dispersoids in the critical temperature range,and grows up most rapidly at the nose temperature of 360℃.The heterogeneous precipitation leads to a low concentration of solute,which consequently reduces the amount of the strengthening phase β＇＇ after aging.In the large-scale industrial production of 6063 alloy,the cooling rate during quenching should be enhanced as high as possible in the quenching sensitive temperature range（410-300℃） to suppress the heterogeneous precipitation to get optimal mechanical properties,and it should be slowed down properly from the solution temperature to 410℃ and below 300℃ to reduce the residual stress.