Graphitized spent carbon cathode(SCC)is a hazardous solid waste generated in the aluminum electrolysis process.In this study,a flotation-acid leaching process is proposed for the purification of graphitized SCC,and th...Graphitized spent carbon cathode(SCC)is a hazardous solid waste generated in the aluminum electrolysis process.In this study,a flotation-acid leaching process is proposed for the purification of graphitized SCC,and the use of the purified SCC as an anode material for lithium-ion batteries is explored.The flotation and acid leaching processes were separately optimized through one-way experiments.The maximum SCC carbon content(93wt%)was achieved at a 90%proportion of−200-mesh flotation particle size,a slurry concentration of 10wt%,a rotation speed of 1600 r/min,and an inflatable capacity of 0.2 m^(3)/h(referred to as FSCC).In the subsequent acid leaching process,the SCC carbon content reached 99.58wt%at a leaching concentration of 5 mol/L,a leaching time of 100 min,a leaching temperature of 85°C,and an HCl/FSCC volume ratio of 5:1.The purified graphitized SCC(referred to as FSCC-CL)was utilized as an anode material,and it exhibited an initial capacity of 348.2 mAh/g at 0.1 C and a reversible capacity of 347.8 mAh/g after 100 cycles.Moreover,compared with commercial graphite,FSCC-CL exhibited better reversibility and cycle stability.Thus,purified SCC is an important candidate for anode material,and the flotation-acid leaching purification method is suitable for the resourceful recycling of SCC.展开更多
Natural graphite is investigated as the cathode for aluminum ion batteries in recent years. However, some drawbacks of the natural graphite such as severe volume swelling shorten its lifetime, In this work, we prepare...Natural graphite is investigated as the cathode for aluminum ion batteries in recent years. However, some drawbacks of the natural graphite such as severe volume swelling shorten its lifetime, In this work, we prepared a composite material by depositing an amorphous carbon on the graphite paper, The composite was used as a cathode to study the electrochemical performance in aluminum ion batteries. The charge/discharge results showed that the composite could exhibit a longer cycle life than the graphite paper, Electrochemical analyses demonstrated that the interface between the amorphous carbon and the graphite paper made a major contribution to the improvement of the cycling stability.展开更多
基金supported by the National Natural Science Foundation of China(No.52274346).
文摘Graphitized spent carbon cathode(SCC)is a hazardous solid waste generated in the aluminum electrolysis process.In this study,a flotation-acid leaching process is proposed for the purification of graphitized SCC,and the use of the purified SCC as an anode material for lithium-ion batteries is explored.The flotation and acid leaching processes were separately optimized through one-way experiments.The maximum SCC carbon content(93wt%)was achieved at a 90%proportion of−200-mesh flotation particle size,a slurry concentration of 10wt%,a rotation speed of 1600 r/min,and an inflatable capacity of 0.2 m^(3)/h(referred to as FSCC).In the subsequent acid leaching process,the SCC carbon content reached 99.58wt%at a leaching concentration of 5 mol/L,a leaching time of 100 min,a leaching temperature of 85°C,and an HCl/FSCC volume ratio of 5:1.The purified graphitized SCC(referred to as FSCC-CL)was utilized as an anode material,and it exhibited an initial capacity of 348.2 mAh/g at 0.1 C and a reversible capacity of 347.8 mAh/g after 100 cycles.Moreover,compared with commercial graphite,FSCC-CL exhibited better reversibility and cycle stability.Thus,purified SCC is an important candidate for anode material,and the flotation-acid leaching purification method is suitable for the resourceful recycling of SCC.
文摘Natural graphite is investigated as the cathode for aluminum ion batteries in recent years. However, some drawbacks of the natural graphite such as severe volume swelling shorten its lifetime, In this work, we prepared a composite material by depositing an amorphous carbon on the graphite paper, The composite was used as a cathode to study the electrochemical performance in aluminum ion batteries. The charge/discharge results showed that the composite could exhibit a longer cycle life than the graphite paper, Electrochemical analyses demonstrated that the interface between the amorphous carbon and the graphite paper made a major contribution to the improvement of the cycling stability.