Diamond-like carbon(DLC)and graphite-like carbon(GLC)coatings have good prospects for improving the surface properties of engine parts.However,further understanding is needed on the effect of working conditions on tri...Diamond-like carbon(DLC)and graphite-like carbon(GLC)coatings have good prospects for improving the surface properties of engine parts.However,further understanding is needed on the effect of working conditions on tribological behaviors.In this study,GLC and two types of DLC coatings were deposited on GCr15 substrate for investigation.The friction and wear properties of self-mated and steel-mated pairs were evaluated.Two temperatures(25 and 90℃),three lubrication conditions(base oil,molybdenum dithiocarbamate(MoDTC)-containing oil,MoDTC+zinc dialkyldithiophosphate(ZDDP)-containing oil),and high Hertz contact stress(2.41 GPa)were applied in the experiments.The results showed that high temperature promoted the effect of ZDDP on steel-mated pairs,but increased wear under base oil lubrication.The increased wear for steel-mated pairs lubricated by MoDTC-containing oil was due to abrasive wear probably caused by MoO_(3) andβ-FeMoO_(4).It was also found that in most cases,the tribological properties of self-mated pairs were better than those of steel-mated pairs.展开更多
Carbon/carbon （C/C） composites were deposited with graphite-like carbon （GLC） coating, and then, Arg-Gly- Asp acid （RGD） peptides were successfully immobilized onto the functionalized GLC coating. GLC coating wa...Carbon/carbon （C/C） composites were deposited with graphite-like carbon （GLC） coating, and then, Arg-Gly- Asp acid （RGD） peptides were successfully immobilized onto the functionalized GLC coating. GLC coating was utilized to prevent carbon particles releasing and create a uniform surface condition for C/C composites. RGD peptides were utilized to improve biocompatibility of GLC coating. Surface chemical characterizations of functionalized GLC coating were detected by contact angle measurement, X-ray photoelectron spectroscopy and Raman spectra. Optical morphology of GLC coatings was observed by confocal laser scanning microscopy. In vitro biological performance was determined using samples seeded with MC3T3-E1 osteoblast-like cells and cultured for 1 week. Surface characterizations and morphological analysis indicated that C/C composites were covered by a dense and uniform GLC coating. Contact angle of GLC coating was reduced to 27.2° when it was functionalized by H202 oxidation at 40 ℃ for 1 h. In vitro cytological test showed that the RGD peptides immobilized GLC coating had a significant improvement in biocompatibility. It was suggested that RGD peptides provided GLC coating with a bioactive surface to improve cell adhesion and proliferation on C/C composites.展开更多
基金This work was supported by the Beijing Municipal Natural Science Foundation(3182032)the National Natural Science Foundation of China(41772389)+1 种基金the Pre-Research Program in National 13th Five-Year Plan(61409230603)Joint Fund of Ministry of Education for Pre-research of Equipment for Young Personnel Project(6141A02033120).
文摘Diamond-like carbon(DLC)and graphite-like carbon(GLC)coatings have good prospects for improving the surface properties of engine parts.However,further understanding is needed on the effect of working conditions on tribological behaviors.In this study,GLC and two types of DLC coatings were deposited on GCr15 substrate for investigation.The friction and wear properties of self-mated and steel-mated pairs were evaluated.Two temperatures(25 and 90℃),three lubrication conditions(base oil,molybdenum dithiocarbamate(MoDTC)-containing oil,MoDTC+zinc dialkyldithiophosphate(ZDDP)-containing oil),and high Hertz contact stress(2.41 GPa)were applied in the experiments.The results showed that high temperature promoted the effect of ZDDP on steel-mated pairs,but increased wear under base oil lubrication.The increased wear for steel-mated pairs lubricated by MoDTC-containing oil was due to abrasive wear probably caused by MoO_(3) andβ-FeMoO_(4).It was also found that in most cases,the tribological properties of self-mated pairs were better than those of steel-mated pairs.
基金supported by the National Natural Science Foundation of China under Grant Nos.51202194 and 51221001the Programme of Introducing Talents of Discipline to Universities(‘‘111’’project of China)under Grant No.B08040
文摘Carbon/carbon （C/C） composites were deposited with graphite-like carbon （GLC） coating, and then, Arg-Gly- Asp acid （RGD） peptides were successfully immobilized onto the functionalized GLC coating. GLC coating was utilized to prevent carbon particles releasing and create a uniform surface condition for C/C composites. RGD peptides were utilized to improve biocompatibility of GLC coating. Surface chemical characterizations of functionalized GLC coating were detected by contact angle measurement, X-ray photoelectron spectroscopy and Raman spectra. Optical morphology of GLC coatings was observed by confocal laser scanning microscopy. In vitro biological performance was determined using samples seeded with MC3T3-E1 osteoblast-like cells and cultured for 1 week. Surface characterizations and morphological analysis indicated that C/C composites were covered by a dense and uniform GLC coating. Contact angle of GLC coating was reduced to 27.2° when it was functionalized by H202 oxidation at 40 ℃ for 1 h. In vitro cytological test showed that the RGD peptides immobilized GLC coating had a significant improvement in biocompatibility. It was suggested that RGD peptides provided GLC coating with a bioactive surface to improve cell adhesion and proliferation on C/C composites.