Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as ou...Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as output power of diode-laser on shear force of micro-joints was studied and the relationship between the shear force and microstructures of micro-joints was analyzed.The results indicate that the formation of intermetallic compound Ag3Sn is the key factor to affect the shear force and the fine eutectic network structures of micro-joints as well as the dispersion morphology of fine compound Ag3Sn,in which eutectic network band is responsible for the improvement of the shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder.With the increases of output power of diode-laser,the shear force and the microstructures change obviously.The eutectic network structures of micro-joints soldered with diode-laser soldering method are more homogeneous and the grains of Ag3Sn compounds are finer in the range of near optimal output power than those soldered with IR reflow soldering method,so the shear force is also higher than that using IR reflow soldering method.When the output power value of diode-laser is about 41.0 W,the shear force exhibits the highest value that is 70% higher than that using IR reflow soldering method.展开更多
Near-infrared(NIR)phosphor-converted light-emitting diodes/laser diodes(LEDs/LDs)are prospective lighting sources for NIR spectroscopy.However,developing NIR phosphor materials with desired thermal robustness and high...Near-infrared(NIR)phosphor-converted light-emitting diodes/laser diodes(LEDs/LDs)are prospective lighting sources for NIR spectroscopy.However,developing NIR phosphor materials with desired thermal robustness and high photoelectric efficiency is a crucial challenge for their applications.In this work,based on the cationic radius matching effect,a series of(Lu,Y)_(3)(Al,Sc,Cr)_(2)Al_(3)O_(12)NIR phosphor ceramics(LuYScCr NIR-PCs)were fabricated by vacuum sintering.Excellent thermal stability(95%@150℃)was obtained in the prepared NIR-PCs,owing to their weak electron-phonon coupling effect(small Huang-Rhys factor).Being excited at 460 nm,NIR-PCs realized a broadband emission(650-850 nm)with internal quantum efficiency(IQE)of 60.68%.Combining NIR-PCs with LED/LD chips,the maximum output power of the encapsulated LED prototype was 447 mW@300 mA with photoelectric efficiency of as high as 18.6%@180 mA,and the maximum output power of the LD prototype was 814 mW@2.5 A.The working temperatures of NIR-PCs were 70.8℃@300 mA(LED)and 102.8℃@3 A(LD).Finally,the prepared NIR-PCs applied in food detection were verified in this study,demonstrating their anticipated application prospects in the future.展开更多
A novel flat-flat resonator consisting of two crystals（Nd：YAG ＋ Nd：YVO4） is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-seg...A novel flat-flat resonator consisting of two crystals（Nd：YAG ＋ Nd：YVO4） is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-segmented（Nd：YAG ＋ Nd：YVO4） and conventional composite（Nd：YAG ＋ Nd：YAG） crystals to demonstrate the feasibility of spectral line matching for output power scale-up in end-pumped lasers. A maximum continuous-wave output power of 79.2 W is reported at 1064 nm, with Mx2= 4.82, My2= 5.48, and a pumping power of 136 W in the multi-segmented crystals（Nd：YAG ＋ Nd：YVO4）. Compared to conventional composite crystals（Nd：YAG ＋ Nd：YAG）, the optical-optical conversion efficiency of multi-segmented crystals（Nd：YAG ＋ Nd：YVO4） from 808 nm to 1064 nm is enhanced from 30% to 58.8%,while the laser output sensitivity as affected by the diode-laser temperature is reduced from 55% to 9%.展开更多
文摘Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as output power of diode-laser on shear force of micro-joints was studied and the relationship between the shear force and microstructures of micro-joints was analyzed.The results indicate that the formation of intermetallic compound Ag3Sn is the key factor to affect the shear force and the fine eutectic network structures of micro-joints as well as the dispersion morphology of fine compound Ag3Sn,in which eutectic network band is responsible for the improvement of the shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder.With the increases of output power of diode-laser,the shear force and the microstructures change obviously.The eutectic network structures of micro-joints soldered with diode-laser soldering method are more homogeneous and the grains of Ag3Sn compounds are finer in the range of near optimal output power than those soldered with IR reflow soldering method,so the shear force is also higher than that using IR reflow soldering method.When the output power value of diode-laser is about 41.0 W,the shear force exhibits the highest value that is 70% higher than that using IR reflow soldering method.
基金The authors acknowledge the generous financial support from the National Natural Science Foundation of China(Nos.52302139,61973103,52272141,and 51972060)Doctoral Foundation Project of Henan University of Technology(No.2021BS069)+3 种基金Natural Science Foundation of Henan Province Youth Fund(No.222300420039)the Key Science and Technology Program of Henan Province(Nos.222102210023 and 232102211074)Project of Songshan Laboratory(No.YYJC072022020)Key Specialized Research of Zhengzhou Science and Technology Innovation Cooperation(No.21ZZXTCX01).
文摘Near-infrared(NIR)phosphor-converted light-emitting diodes/laser diodes(LEDs/LDs)are prospective lighting sources for NIR spectroscopy.However,developing NIR phosphor materials with desired thermal robustness and high photoelectric efficiency is a crucial challenge for their applications.In this work,based on the cationic radius matching effect,a series of(Lu,Y)_(3)(Al,Sc,Cr)_(2)Al_(3)O_(12)NIR phosphor ceramics(LuYScCr NIR-PCs)were fabricated by vacuum sintering.Excellent thermal stability(95%@150℃)was obtained in the prepared NIR-PCs,owing to their weak electron-phonon coupling effect(small Huang-Rhys factor).Being excited at 460 nm,NIR-PCs realized a broadband emission(650-850 nm)with internal quantum efficiency(IQE)of 60.68%.Combining NIR-PCs with LED/LD chips,the maximum output power of the encapsulated LED prototype was 447 mW@300 mA with photoelectric efficiency of as high as 18.6%@180 mA,and the maximum output power of the LD prototype was 814 mW@2.5 A.The working temperatures of NIR-PCs were 70.8℃@300 mA(LED)and 102.8℃@3 A(LD).Finally,the prepared NIR-PCs applied in food detection were verified in this study,demonstrating their anticipated application prospects in the future.
基金Project supported by the National Defense Pre-Research Foundation of China(Grant No.9140A020105)
文摘A novel flat-flat resonator consisting of two crystals（Nd：YAG ＋ Nd：YVO4） is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-segmented（Nd：YAG ＋ Nd：YVO4） and conventional composite（Nd：YAG ＋ Nd：YAG） crystals to demonstrate the feasibility of spectral line matching for output power scale-up in end-pumped lasers. A maximum continuous-wave output power of 79.2 W is reported at 1064 nm, with Mx2= 4.82, My2= 5.48, and a pumping power of 136 W in the multi-segmented crystals（Nd：YAG ＋ Nd：YVO4）. Compared to conventional composite crystals（Nd：YAG ＋ Nd：YAG）, the optical-optical conversion efficiency of multi-segmented crystals（Nd：YAG ＋ Nd：YVO4） from 808 nm to 1064 nm is enhanced from 30% to 58.8%,while the laser output sensitivity as affected by the diode-laser temperature is reduced from 55% to 9%.