A study was conducted for metal extraction from copper smelting dust using the oxidation leaching and control of potential technology.The effects of H2O2 dosage,H2O2 feeding speed,initial HCl concentration,leaching te...A study was conducted for metal extraction from copper smelting dust using the oxidation leaching and control of potential technology.The effects of H2O2 dosage,H2O2 feeding speed,initial HCl concentration,leaching temperature,liquid-to-solid ratio and leaching time on metals leaching efficiencies were investigated.The following optimized leaching conditions were obtained:H2O2 dosage of 0.8 mL/g(redox potential of 429 mV),H2O2 feeding speed of 1.0 mL/min,initial H2SO4 concentration of 1.0 mol/L,initial HCl concentration of 1.0 mol/L,leaching temperature of 80°C,initial liquid-to-solid ratio of 5:1 mL/g and leaching time of 1.5 h.Under the optimized conditions,copper and arsenic can be effectively leached from copper smelting dust,leaving residue as a suitable lead resource.The average leaching efficiencies of copper,arsenic and iron are 95.27%,96.82%and 46.65%,respectively.展开更多
The application of pressure leaching technology in the treatment of high-copper and high-arsenic dust was studied.The pressure leaching technique was determined as follows:the liquid to solid ratio(mL/g)of 5:1,the lea...The application of pressure leaching technology in the treatment of high-copper and high-arsenic dust was studied.The pressure leaching technique was determined as follows:the liquid to solid ratio(mL/g)of 5:1,the leaching temperature of 453 K,the retention time of 2 h,the initial sulfuric acid concentration of 0.74 mol/L,the oxygen partial pressure of 0.7 MPa,and the agitation speed of 500 r/min.Under these conditions,95%of copper and 99%of zinc and only 6%of iron in the dust were leached,while about 20%of arsenic was also leached.The leaching technique was optimized further to restrain the leaching of arsenic by adding a small quantity of ferrous iron into the leaching system(c(Fe2 +)=0.036 mol/L).Copper and zinc can be effectively separated from arsenic and iron in the leach.The optimal pressure leaching technique of high-copper and high-arsenic smelter dust is proved to be effective.展开更多
基金Project(2016M602427)supported by the Postdoctoral Science Foundation of ChinaProject supported by the Fundamental Research Funds for the Central Universities of Central South University,China
文摘A study was conducted for metal extraction from copper smelting dust using the oxidation leaching and control of potential technology.The effects of H2O2 dosage,H2O2 feeding speed,initial HCl concentration,leaching temperature,liquid-to-solid ratio and leaching time on metals leaching efficiencies were investigated.The following optimized leaching conditions were obtained:H2O2 dosage of 0.8 mL/g(redox potential of 429 mV),H2O2 feeding speed of 1.0 mL/min,initial H2SO4 concentration of 1.0 mol/L,initial HCl concentration of 1.0 mol/L,leaching temperature of 80°C,initial liquid-to-solid ratio of 5:1 mL/g and leaching time of 1.5 h.Under the optimized conditions,copper and arsenic can be effectively leached from copper smelting dust,leaving residue as a suitable lead resource.The average leaching efficiencies of copper,arsenic and iron are 95.27%,96.82%and 46.65%,respectively.
文摘The application of pressure leaching technology in the treatment of high-copper and high-arsenic dust was studied.The pressure leaching technique was determined as follows:the liquid to solid ratio(mL/g)of 5:1,the leaching temperature of 453 K,the retention time of 2 h,the initial sulfuric acid concentration of 0.74 mol/L,the oxygen partial pressure of 0.7 MPa,and the agitation speed of 500 r/min.Under these conditions,95%of copper and 99%of zinc and only 6%of iron in the dust were leached,while about 20%of arsenic was also leached.The leaching technique was optimized further to restrain the leaching of arsenic by adding a small quantity of ferrous iron into the leaching system(c(Fe2 +)=0.036 mol/L).Copper and zinc can be effectively separated from arsenic and iron in the leach.The optimal pressure leaching technique of high-copper and high-arsenic smelter dust is proved to be effective.
