PLGA thin films were prepared onto implantable devices by the electrospray and pressurized spray method. Thin films with structural gradients were obtained by controlling four parameters consisting of solution conce...PLGA thin films were prepared onto implantable devices by the electrospray and pressurized spray method. Thin films with structural gradients were obtained by controlling four parameters consisting of solution concentration, applied voltage, air pressure , and deposition time. The surface morphologies of the deposited films were observed using scanning electron microscopy （SEM）. The image analysis revealed the control factors on the preparation of PLGA thin films. The beaded structure is ensily formed with a decrease in polymer concentration while the fibrous structure is easily formed with an increuse in polymer concentration. With the increase in applied voltage, the surface morphologies changed continnously from a small amount of fibrous shape to a large fibrous one： a small amount of.fibrous shape at 10 kV, more fibers with non-uniform diameter at 20 kV, and most fibers with uniform diameter at 30 kV. Low air pressure（0.1 MPa ） corresponded to round particles while high air pressure （0.3 MPa ） corresponded to fiat particles. The change in thickness from 5.34 to 10.1μm was a result of deposition time increasing from 5 to 10 s. From our above work, films of the bead or fiber structures can be obtained by changing electrical parameters to impropvc tbe biocompntibility of the film.展开更多
Background The most important objective of transplant studies in the injured spinal cord has been to provide a favorable environment for axonal growth. Moreover, the continuing discovery of new grafts is providing new...Background The most important objective of transplant studies in the injured spinal cord has been to provide a favorable environment for axonal growth. Moreover, the continuing discovery of new grafts is providing new potentially interesting transplant candidates. Our purpose was to observe the morphological and functional repair effects of the co-transplantation of neural stem cell （NSC）, Schwann ceils （SCs） and poly lactide-co-glycolide acid （PLGA） on the spinal cord injury of rats.Methods A scaffold of PLGA was fabricated. NSCs and SCs were cultured, with the NSCs labeled with 5-bromodeoxyuridine, and the complex of NSC/PLGA or NSC＋SCs/PLGA were constructed. Thirty-six Wistar rats were randomly divided into three groups： group A （transplantation of PLGA）, group B （transplantation of NSC/PLGA） and group C （transplantation of NSC＋SCs/PLGA）. The 3 mm length of the right hemicord was removed under the microscope in all rats. The PLGA or the complex of PLGA-celIs were implanted into the injury site. Basso-Beattie-Bresnahan （BBB）locomotion scores, motor and somatosensory evoked potential of lower limbs were examined to learn the rehabilitation of sensory and motor function at 4 weeks, 8 weeks, 12 weeks and 24 weeks after injury. All the recovered spinal cord injury （SCI） tissues were observed with HE staining, immunohistochemistry, and transelectronmicroscopy to identify the survival, migration and differentiation of the transplanted cells and the regeneration of neural fibres at 4 weeks, 8 weeks,12 weeks and 24 weeks after injury.Results （1） From 4 weeks to 24 weeks after injury, the BBB locomotion scores of cell-transplanted groups were better than those of the non-cell-transplanted group, especially group C （P 〈0.05）. The amplitudes of the somatosensory evoked potential （SEP） and motor-evoked potential （MEP） were improved after injury in groups B and C, but the amplitude of SEP and MEP at 4 weeks was lower than that at 12 weeks and 24 weeks after injury. Com展开更多
A new biomimetic bone tissue engineering scaffold material, nano-HAI PLGA-（ PEG-Asp ）n composite, was synthesized by a biologically inspired self-assembling approach. A novel biodegradable PLGA- （ PEG-Asp ）n cop...A new biomimetic bone tissue engineering scaffold material, nano-HAI PLGA-（ PEG-Asp ）n composite, was synthesized by a biologically inspired self-assembling approach. A novel biodegradable PLGA- （ PEG-Asp ）n copolymer with pendant amine functional groups and enhanced hydrophilicity woo synthesized by bulk ring-opening copolymerization by DL-lactide（ DLLA） and glycolide（ GA ） with Aspartic acid （ Asp ）-Polyethylene glycol（PEG） alt-prepolymer. A Three-dimensional, porous scaffold of the PLGA-（ PEG- Asp）n copolymer was fabricated by a solvent casting , particulate leaching process. The scaffold woo then incubated in modified simulated body fluid （naSBF）. Growth of HA nanocrystals on the inner pore surfaces of the porous scaffold is confirmed by calcium ion binding analyses, SEM , mass increooe meoourements and quantification of phosphate content within scaffolds. SEM analysis demonstrated the nucleation and growth of a continuous bonelike, low crystalline carbonated HA nanocrystals on the inner pore surfaces of the PLGA- （ PEG-Asp ）n scaffolds. The amount of calcium binding, total mass and the mass of phosphate on experimental PLGA- （ PEG-Asp ） n scaffolds at different incubation times in mSBF was significantly greater than that of control PLGA scaffolds. This nano-HA/ PLGA-（ PEG- Asp ）n composite stunts some features of natural bone both in main composition and hierarchical microstrueture. The Asp- PEG alt-prepolymer modified PleA copolymer provide a controllable high surface density and distribution of anionic functional groups which would enhance nucleation and growth of bonelike mineral following exposure to mSBF. This biomimetic treatment provides a simple method for surface functionalization and sabsequent mineral nucleation and self-oosembling on bodegradable polymer scaffolds for tissue engineering.展开更多
文摘PLGA thin films were prepared onto implantable devices by the electrospray and pressurized spray method. Thin films with structural gradients were obtained by controlling four parameters consisting of solution concentration, applied voltage, air pressure , and deposition time. The surface morphologies of the deposited films were observed using scanning electron microscopy （SEM）. The image analysis revealed the control factors on the preparation of PLGA thin films. The beaded structure is ensily formed with a decrease in polymer concentration while the fibrous structure is easily formed with an increuse in polymer concentration. With the increase in applied voltage, the surface morphologies changed continnously from a small amount of fibrous shape to a large fibrous one： a small amount of.fibrous shape at 10 kV, more fibers with non-uniform diameter at 20 kV, and most fibers with uniform diameter at 30 kV. Low air pressure（0.1 MPa ） corresponded to round particles while high air pressure （0.3 MPa ） corresponded to fiat particles. The change in thickness from 5.34 to 10.1μm was a result of deposition time increasing from 5 to 10 s. From our above work, films of the bead or fiber structures can be obtained by changing electrical parameters to impropvc tbe biocompntibility of the film.
基金This work was supported by grants from the National Natural Science Foundation of China （No. 30370543, No. 30540450581）.
文摘Background The most important objective of transplant studies in the injured spinal cord has been to provide a favorable environment for axonal growth. Moreover, the continuing discovery of new grafts is providing new potentially interesting transplant candidates. Our purpose was to observe the morphological and functional repair effects of the co-transplantation of neural stem cell （NSC）, Schwann ceils （SCs） and poly lactide-co-glycolide acid （PLGA） on the spinal cord injury of rats.Methods A scaffold of PLGA was fabricated. NSCs and SCs were cultured, with the NSCs labeled with 5-bromodeoxyuridine, and the complex of NSC/PLGA or NSC＋SCs/PLGA were constructed. Thirty-six Wistar rats were randomly divided into three groups： group A （transplantation of PLGA）, group B （transplantation of NSC/PLGA） and group C （transplantation of NSC＋SCs/PLGA）. The 3 mm length of the right hemicord was removed under the microscope in all rats. The PLGA or the complex of PLGA-celIs were implanted into the injury site. Basso-Beattie-Bresnahan （BBB）locomotion scores, motor and somatosensory evoked potential of lower limbs were examined to learn the rehabilitation of sensory and motor function at 4 weeks, 8 weeks, 12 weeks and 24 weeks after injury. All the recovered spinal cord injury （SCI） tissues were observed with HE staining, immunohistochemistry, and transelectronmicroscopy to identify the survival, migration and differentiation of the transplanted cells and the regeneration of neural fibres at 4 weeks, 8 weeks,12 weeks and 24 weeks after injury.Results （1） From 4 weeks to 24 weeks after injury, the BBB locomotion scores of cell-transplanted groups were better than those of the non-cell-transplanted group, especially group C （P 〈0.05）. The amplitudes of the somatosensory evoked potential （SEP） and motor-evoked potential （MEP） were improved after injury in groups B and C, but the amplitude of SEP and MEP at 4 weeks was lower than that at 12 weeks and 24 weeks after injury. Com
文摘A new biomimetic bone tissue engineering scaffold material, nano-HAI PLGA-（ PEG-Asp ）n composite, was synthesized by a biologically inspired self-assembling approach. A novel biodegradable PLGA- （ PEG-Asp ）n copolymer with pendant amine functional groups and enhanced hydrophilicity woo synthesized by bulk ring-opening copolymerization by DL-lactide（ DLLA） and glycolide（ GA ） with Aspartic acid （ Asp ）-Polyethylene glycol（PEG） alt-prepolymer. A Three-dimensional, porous scaffold of the PLGA-（ PEG- Asp）n copolymer was fabricated by a solvent casting , particulate leaching process. The scaffold woo then incubated in modified simulated body fluid （naSBF）. Growth of HA nanocrystals on the inner pore surfaces of the porous scaffold is confirmed by calcium ion binding analyses, SEM , mass increooe meoourements and quantification of phosphate content within scaffolds. SEM analysis demonstrated the nucleation and growth of a continuous bonelike, low crystalline carbonated HA nanocrystals on the inner pore surfaces of the PLGA- （ PEG-Asp ）n scaffolds. The amount of calcium binding, total mass and the mass of phosphate on experimental PLGA- （ PEG-Asp ） n scaffolds at different incubation times in mSBF was significantly greater than that of control PLGA scaffolds. This nano-HA/ PLGA-（ PEG- Asp ）n composite stunts some features of natural bone both in main composition and hierarchical microstrueture. The Asp- PEG alt-prepolymer modified PleA copolymer provide a controllable high surface density and distribution of anionic functional groups which would enhance nucleation and growth of bonelike mineral following exposure to mSBF. This biomimetic treatment provides a simple method for surface functionalization and sabsequent mineral nucleation and self-oosembling on bodegradable polymer scaffolds for tissue engineering.