Because of the complex constraint effects among layers in multi-layered metallic bellows hydroforming,the stress concentration and defects such as wrinkling and fracture may easily occur.It is a key to reveal the defo...Because of the complex constraint effects among layers in multi-layered metallic bellows hydroforming,the stress concentration and defects such as wrinkling and fracture may easily occur.It is a key to reveal the deformation behaviors in order to obtain a sound product.Based on the ABAQUS platform,a 3 D-FE model of the four-layered U-shaped metallic bellow hydroforming process is established and validated by experiment.The stress and strain distributions,wall thickness variations and bellow profiles of each layer in the whole process,including bulging,folding and springback stages,are studied.Then deformation behaviors of bellows under different forming conditions are discussed.It is found that the wall thinning degrees of different layer vary after hydroforming,and is the largest for the inner layer and smallest for the outer layer.At folding stage,the wall thinning degree of the crown point increases lineally,and the difference among layers increases as the process going.The displacements of the crown point decrease from the inner layer to the outer layer.After springback,the U-shaped cross section changes to a tongue shape,the change of convolution pitch is much larger than the change of convolution height,and the springback values of the inner layer are smaller than the outer layer.An increase in the internal pressure and die spacing cause the maximum wall thinning degree and springback increase.With changing of process parameters,bellows with deep convolution are easily encountered wall thinning during hydroforming and convolution distortion after springback.This research is helpful for precision forming of multi-layered bellows.展开更多
基金the funds of the National Natural Science Foundation of China(No.51875456)the Natural Science Basic Research Plan in Shaanxi Province of China(No.2019JM-450)+3 种基金the Young Talent fund of University Association for Science and Technology in Shaanxi,China(No.20170518)the Key Laboratory of Advanced Manufacture Technology for Automobile Parts(Chongqing University of Technology),Ministry of Education(No.2018KLMT03)Materials Science and Engineering provincial-level superior discipline funding project of Xi'an Shiyou Universitythe Program for Young Innovative Research Team in Xi'an Shiyou University(No.2015QNKYCXTD02)。
文摘Because of the complex constraint effects among layers in multi-layered metallic bellows hydroforming,the stress concentration and defects such as wrinkling and fracture may easily occur.It is a key to reveal the deformation behaviors in order to obtain a sound product.Based on the ABAQUS platform,a 3 D-FE model of the four-layered U-shaped metallic bellow hydroforming process is established and validated by experiment.The stress and strain distributions,wall thickness variations and bellow profiles of each layer in the whole process,including bulging,folding and springback stages,are studied.Then deformation behaviors of bellows under different forming conditions are discussed.It is found that the wall thinning degrees of different layer vary after hydroforming,and is the largest for the inner layer and smallest for the outer layer.At folding stage,the wall thinning degree of the crown point increases lineally,and the difference among layers increases as the process going.The displacements of the crown point decrease from the inner layer to the outer layer.After springback,the U-shaped cross section changes to a tongue shape,the change of convolution pitch is much larger than the change of convolution height,and the springback values of the inner layer are smaller than the outer layer.An increase in the internal pressure and die spacing cause the maximum wall thinning degree and springback increase.With changing of process parameters,bellows with deep convolution are easily encountered wall thinning during hydroforming and convolution distortion after springback.This research is helpful for precision forming of multi-layered bellows.
