基于对符合再生要求的材料充分回收利用,节约资源、降低排放及减少传统半刚性基层沥青路面反射裂缝的理念,G30连霍高速郑洛段大修改建工程将传统的半刚性基层替换为偏柔性的双层乳化沥青厂拌冷再生基层结构,通过全新的双层乳化沥青厂拌...基于对符合再生要求的材料充分回收利用,节约资源、降低排放及减少传统半刚性基层沥青路面反射裂缝的理念,G30连霍高速郑洛段大修改建工程将传统的半刚性基层替换为偏柔性的双层乳化沥青厂拌冷再生基层结构,通过全新的双层乳化沥青厂拌冷再生路面结构设计、沥青混合料回收料(RAP)性能分析、乳化沥青厂拌冷再生配合比设计、现场取芯与弯沉检测性能验证及乳化剂性能改善,确定并验证了最佳路用性能下的混合料生产配合比。结果表明:当0~10 mm RAP掺量32%,10 mm~30 mm RAP掺量43%,0~5 mm石屑掺量12%,10 mm~30 mm碎石掺量13%,乳化沥青用量4.1%,水泥用量1.8%,最佳含水率为5.2%时,混合料路用性能最佳,其15℃劈裂强度达0.625 MPa;双层乳化沥青厂拌冷再生基层结构对沥青混合料回收料利用率高、经济效益明显。展开更多
Warm-mix asphalt(WMA) technology was applied for asphalt mixture,plant-produced porous WMA using LEADCAP additive(porous WMA-LEADCAP) test section was built and compacted at 30℃ lower than porous hot-mix asphalt(poro...Warm-mix asphalt(WMA) technology was applied for asphalt mixture,plant-produced porous WMA using LEADCAP additive(porous WMA-LEADCAP) test section was built and compacted at 30℃ lower than porous hot-mix asphalt(porous HMA) test section.Marshall mix designs were conducted for porous WMA-LEADCAP mixture and porous HMA mixture in terms of Marshall stability,Cantabro loss and dynamic stability.The workability,compactablity and surface quality of porous WMA-LEADCAP pavement were investigated,and the engineering properties of plant-produced porous WMA-LEADCAP mixture and plant-produced porous HMA mixture were evaluated based on indirect tensile strength test and dynamic immersion test.Analysis result shows that LEADCAP additive does not affect polymermodified asphalt in terms of penetration,softening point,viscosity,ductility,toughness and tenacity.Porous WMA-LEADCAP pavement has similar field density,permeability and smoothness compared with standard porous HMA pavement.Plant-produced porous WMA-LEADCAP mixture is equivalent to plantproduced porous HMA mixture in indirect tensile strength,toughness and stripping resistance.4tabs,4figs,9refs.展开更多
文摘基于对符合再生要求的材料充分回收利用,节约资源、降低排放及减少传统半刚性基层沥青路面反射裂缝的理念,G30连霍高速郑洛段大修改建工程将传统的半刚性基层替换为偏柔性的双层乳化沥青厂拌冷再生基层结构,通过全新的双层乳化沥青厂拌冷再生路面结构设计、沥青混合料回收料(RAP)性能分析、乳化沥青厂拌冷再生配合比设计、现场取芯与弯沉检测性能验证及乳化剂性能改善,确定并验证了最佳路用性能下的混合料生产配合比。结果表明:当0~10 mm RAP掺量32%,10 mm~30 mm RAP掺量43%,0~5 mm石屑掺量12%,10 mm~30 mm碎石掺量13%,乳化沥青用量4.1%,水泥用量1.8%,最佳含水率为5.2%时,混合料路用性能最佳,其15℃劈裂强度达0.625 MPa;双层乳化沥青厂拌冷再生基层结构对沥青混合料回收料利用率高、经济效益明显。
基金Strategic Research Project (Development of Low-Carbon and Low-Cost Asphalt Pavements)Funded by Korea Institute of Construction Technology
文摘Warm-mix asphalt(WMA) technology was applied for asphalt mixture,plant-produced porous WMA using LEADCAP additive(porous WMA-LEADCAP) test section was built and compacted at 30℃ lower than porous hot-mix asphalt(porous HMA) test section.Marshall mix designs were conducted for porous WMA-LEADCAP mixture and porous HMA mixture in terms of Marshall stability,Cantabro loss and dynamic stability.The workability,compactablity and surface quality of porous WMA-LEADCAP pavement were investigated,and the engineering properties of plant-produced porous WMA-LEADCAP mixture and plant-produced porous HMA mixture were evaluated based on indirect tensile strength test and dynamic immersion test.Analysis result shows that LEADCAP additive does not affect polymermodified asphalt in terms of penetration,softening point,viscosity,ductility,toughness and tenacity.Porous WMA-LEADCAP pavement has similar field density,permeability and smoothness compared with standard porous HMA pavement.Plant-produced porous WMA-LEADCAP mixture is equivalent to plantproduced porous HMA mixture in indirect tensile strength,toughness and stripping resistance.4tabs,4figs,9refs.
