The effects of minor Sc and Zr additions on the mechanical properties and microstructure evolution of Al Zn Mg Cu alloys were studied using tensile tests, scanning electron microscopy (SEM) and transmission electron m...The effects of minor Sc and Zr additions on the mechanical properties and microstructure evolution of Al Zn Mg Cu alloys were studied using tensile tests, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The ultimate tensile strength of the peak-aged Al Zn Mg Cu alloy is improved by about 105 MPa with the addition of 0.10% Zr. An increase of about 133 MPa is observed with the joint addition of 0.07% Sc and 0.07% Zr. For the alloys modified with the minor addition of Sc and Zr (0.14%), the main strengthening mechanisms of minor addition of Sc and Zr are fine-grain strengthening, sub-structure strengthening and the Orowan strengthening mechanism produced by the Al3(Sc,Zr) and Al3Zr dispersoids. The volume of Al3Zr particles is less than that of Al3(Sc,Zr) particles, but the distribution of Al3(Sc,Zr) particles is more dispersed throughout the matrix leading to pinning the dislocations motion and restraining the recrystallization more effectively.展开更多
Three kinds of Al-Zn-Mg-Cu based alloys with 0.22%, 0.36%(Sc+Zr) (mass fraction, %), and without Sc, Zr addition were prepared by ingot metallurgy. By using optical microscopy, transmission electronic microscopy and s...Three kinds of Al-Zn-Mg-Cu based alloys with 0.22%, 0.36%(Sc+Zr) (mass fraction, %), and without Sc, Zr addition were prepared by ingot metallurgy. By using optical microscopy, transmission electronic microscopy and scanning electron microscopy, the effects of microalloying elements of Sc, Zr on the microstructure of super-high-strength Al-Zn-Mg-Cu alloys related to mechanical properties were investigated. The tensile properties and microstructures of the studied alloys under different heat treatment conditions were studied. The addition of minor Sc, Zr results in the formation of Al3(Sc,Zr) particles. These particles are highly effective in refining the microstructures, retarding recrystallization, pinning dislocations and subboundaries. The strength of Al-Zn-Mg-Cu alloys was greatly improved by simultaneously adding minor Sc, Zr, meanwhile the ductility of the studied alloys remains at a higher level. The 0.36%(Sc+Zr) alloys gain the optimal properties after 465 ℃/h solution and 120 ℃/24 h aging. The increment of strength is mainly due to strengthening of fine grain and substructure and precipitation of Al3(Sc, Zr) particles.展开更多
The Zn,Cu,and Sc contents of 7xxx Al alloys were adjusted according to the chemical composition of a 7085 Al alloy,and the effects of Zn and Cu contents and Sc addition on the microstructures,hardness,and quench sensi...The Zn,Cu,and Sc contents of 7xxx Al alloys were adjusted according to the chemical composition of a 7085 Al alloy,and the effects of Zn and Cu contents and Sc addition on the microstructures,hardness,and quench sensitivity of the 7xxx Al alloys were studied.The alloys with high Zn content and Sc addition exhibited higher hardness than the 7085 alloy at the position 3 mm away from the quenching end.The density ofηand T phases increased with the increase in Zn and Cu contents,and the Sc addition led to the formation of the Y phase and moreηphases at the position 120 mm away from the quenching end.Compared with the 7085 alloy,the high Zn−high Cu and Sc-added alloys exhibited higher quench sensitivity,while the simultaneous increase in Zn content and decrease in Cu content could enhance the hardness and reduce the quench sensitivity of the 7085 alloy.展开更多
基金Project (2016B090931004) supported by the Scientific and Research Plan of Guangdong Province, ChinaProject (51601229) supported by the National Natural Science Foundation of China。
文摘The effects of minor Sc and Zr additions on the mechanical properties and microstructure evolution of Al Zn Mg Cu alloys were studied using tensile tests, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The ultimate tensile strength of the peak-aged Al Zn Mg Cu alloy is improved by about 105 MPa with the addition of 0.10% Zr. An increase of about 133 MPa is observed with the joint addition of 0.07% Sc and 0.07% Zr. For the alloys modified with the minor addition of Sc and Zr (0.14%), the main strengthening mechanisms of minor addition of Sc and Zr are fine-grain strengthening, sub-structure strengthening and the Orowan strengthening mechanism produced by the Al3(Sc,Zr) and Al3Zr dispersoids. The volume of Al3Zr particles is less than that of Al3(Sc,Zr) particles, but the distribution of Al3(Sc,Zr) particles is more dispersed throughout the matrix leading to pinning the dislocations motion and restraining the recrystallization more effectively.
基金Project(2002AA305104) supported by the National High-Tech Research and Development Program of China
文摘Three kinds of Al-Zn-Mg-Cu based alloys with 0.22%, 0.36%(Sc+Zr) (mass fraction, %), and without Sc, Zr addition were prepared by ingot metallurgy. By using optical microscopy, transmission electronic microscopy and scanning electron microscopy, the effects of microalloying elements of Sc, Zr on the microstructure of super-high-strength Al-Zn-Mg-Cu alloys related to mechanical properties were investigated. The tensile properties and microstructures of the studied alloys under different heat treatment conditions were studied. The addition of minor Sc, Zr results in the formation of Al3(Sc,Zr) particles. These particles are highly effective in refining the microstructures, retarding recrystallization, pinning dislocations and subboundaries. The strength of Al-Zn-Mg-Cu alloys was greatly improved by simultaneously adding minor Sc, Zr, meanwhile the ductility of the studied alloys remains at a higher level. The 0.36%(Sc+Zr) alloys gain the optimal properties after 465 ℃/h solution and 120 ℃/24 h aging. The increment of strength is mainly due to strengthening of fine grain and substructure and precipitation of Al3(Sc, Zr) particles.
基金The authors are grateful for the financial supports from the Science and Technology Major Project of Guangxi,China(GKAA17202007).
文摘The Zn,Cu,and Sc contents of 7xxx Al alloys were adjusted according to the chemical composition of a 7085 Al alloy,and the effects of Zn and Cu contents and Sc addition on the microstructures,hardness,and quench sensitivity of the 7xxx Al alloys were studied.The alloys with high Zn content and Sc addition exhibited higher hardness than the 7085 alloy at the position 3 mm away from the quenching end.The density ofηand T phases increased with the increase in Zn and Cu contents,and the Sc addition led to the formation of the Y phase and moreηphases at the position 120 mm away from the quenching end.Compared with the 7085 alloy,the high Zn−high Cu and Sc-added alloys exhibited higher quench sensitivity,while the simultaneous increase in Zn content and decrease in Cu content could enhance the hardness and reduce the quench sensitivity of the 7085 alloy.