Visible photoactive AgBr/TiO2 was immobilized on a SiO2@Fe3O4 magnetic support by solvother- rnal and sol-gel methods to form a AgBr-TiO2/SiO2@Fe3O4 magnetic photocatalyst. Samples were characterized by X-ray diffract...Visible photoactive AgBr/TiO2 was immobilized on a SiO2@Fe3O4 magnetic support by solvother- rnal and sol-gel methods to form a AgBr-TiO2/SiO2@Fe3O4 magnetic photocatalyst. Samples were characterized by X-ray diffraction, high-resolution transmission electron microscopy and magne- tometry. Hereto-structured AgBr/TiO2 was well seeded on the shell-core SiO2@Fe3O4 structure. The AgBr-TiO2/SiO2@Fe3O4 magnetic photocatalyst exhibited high photocatalytic activity in the degrada- tion of methylene blue under visible light. The photocatalyst was superparamagnetic, which is beneficial for facile magnetic separation.展开更多
A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic re...A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic reduction（SCR） performance and SO2-resistant ability of TiO2-SiO2-WO3 were greatly enhanced by the introduction of cerium. The catalyst containing 10% CeO2 showed the highest NO conversion in a wide temperature range and good N2 selectivity with broad operation temperature window at the gas hourly space velocity（GHSV） of 30000 h–1, which was a very promising catalyst for NOx abatement from diesel engine exhaust. The catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy with energy dispersive X-ray spectroscopy（SEM-EDS）, N2 adsorption-desorption（BET） and X-ray photoelectron spectroscopy（XPS）. The characterization results showed that the bigger pore radius, higher surface atomic concentration and dispersion of Ce and the abundant adsorbed oxygen on the surface of catalyst contributed to the best NH3-SCR performance of CeO2/TiO2-SiO2-WO3 catalyst containing 10% CeO2.展开更多
文摘以溶胶-凝胶法和浸渍法制备V2O5/TiO2-SiO2催化剂,将其应用于甲醇与乙醇一步合成异丁醛的催化反应,并采用BET、XRDI、R测试技术对催化剂的结构进行表征,考察制备方法和焙烧温度对催化剂结构和催化性能的影响.结果表明:采用溶胶-凝胶法制备的催化剂具有较好的催化性能,适宜的焙烧温度为773 K.
基金financial support from the National Natural Science Foundation of China(10972025,10972039,11172043)the State Key Laboratory of Explosion Science and Technology,Beijing Institute of Technology(KFJJ11-6M)the Guangdong Provincial R&D Program(2011B090400419)
文摘Visible photoactive AgBr/TiO2 was immobilized on a SiO2@Fe3O4 magnetic support by solvother- rnal and sol-gel methods to form a AgBr-TiO2/SiO2@Fe3O4 magnetic photocatalyst. Samples were characterized by X-ray diffraction, high-resolution transmission electron microscopy and magne- tometry. Hereto-structured AgBr/TiO2 was well seeded on the shell-core SiO2@Fe3O4 structure. The AgBr-TiO2/SiO2@Fe3O4 magnetic photocatalyst exhibited high photocatalytic activity in the degrada- tion of methylene blue under visible light. The photocatalyst was superparamagnetic, which is beneficial for facile magnetic separation.
基金supported by the National Natural Science Foundation of China(21173153)the National High Technology Research and Development Program of China(863 project)(2013AA065304)
文摘A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic reduction（SCR） performance and SO2-resistant ability of TiO2-SiO2-WO3 were greatly enhanced by the introduction of cerium. The catalyst containing 10% CeO2 showed the highest NO conversion in a wide temperature range and good N2 selectivity with broad operation temperature window at the gas hourly space velocity（GHSV） of 30000 h–1, which was a very promising catalyst for NOx abatement from diesel engine exhaust. The catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy with energy dispersive X-ray spectroscopy（SEM-EDS）, N2 adsorption-desorption（BET） and X-ray photoelectron spectroscopy（XPS）. The characterization results showed that the bigger pore radius, higher surface atomic concentration and dispersion of Ce and the abundant adsorbed oxygen on the surface of catalyst contributed to the best NH3-SCR performance of CeO2/TiO2-SiO2-WO3 catalyst containing 10% CeO2.