The room-temperature stability of the retained austenite against strain-induced martensitic transformation, its deformation behavior, the response to the bainitic isothermal treatment, the appearance of yield point el...The room-temperature stability of the retained austenite against strain-induced martensitic transformation, its deformation behavior, the response to the bainitic isothermal treatment, the appearance of yield point elongation and other peculiarities of plastic flow, and the mechanical properties of transformation-induced plasticity（TRIP） steel were tailored based on the chemical homogeneity and the relative distribution of the retained austenite, bainite, and ferrite in the microstructure. The presence of ferritic-pearlitic banded structure in the initial microstructure resulted in an inhomogeneous TRIP microstructure, in which the retained austenite and bainite were confined to some bands and it was found to be responsible for the resultant inferior mechanical properties. The appearance of discontinuous yielding for the chemically inhomogeneous material was related to the martensitic transformation of unstable retained austenite at the initial stage of tensile deformation. These results are essential for better understanding of the behavior of advanced high-strength steels and their applications.展开更多
In the present study, a quenching treatment prior to two-stage heat treatment was conducted on a Fe-0.28C-1.55Mn-2.06Al transformation-induced plasticity steel to tailor the final microstructure. Compared with the mic...In the present study, a quenching treatment prior to two-stage heat treatment was conducted on a Fe-0.28C-1.55Mn-2.06Al transformation-induced plasticity steel to tailor the final microstructure. Compared with the microstructure of the ferrite, bainite and blocky retained austenite obtained by conventional two-stage heat treatment, the microstructure subjected to quenching plus two-stage heat treatment was composed of the ferrite, lath bainite and film-like retained austenite. The corresponding tensile behavior and mechanical stability of retained austenite were investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The results show that the mechanical stability of blocky retained austenite grains is lower and most of them transform to martensite during the tensile deformation, which leads to higher ultimate tensile strength and instantaneous work hardening exponent. Film-like retained austenite has relatively higher stability, which could cause sustained work hardening and high ductility as well as product of strength and elongation.展开更多
The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation an...The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation and transformation-induced plasticity behavior of retained austenite were analyzed.The results show that with multipass deformation,reduction per pass of more than critical deformation in austenite recrystallization region and total reduction of more than 58% in non-recrystallization region and high temperature section of two-phase region,austenite can be refined before γ→α transformation.It is beneficial to obtain refined ferrite grain in final microstructure.To obtain fine and uniform microstructure and excellent strength-ductility balance,a three-stage cooling process（laminar cooling-air cooling-ultra-fast cooling）after hot rolling was conducted.The ultimate tensile strength and elongation of the investigated steel can reach 663 MPa and 41%,respectively.展开更多
文摘The room-temperature stability of the retained austenite against strain-induced martensitic transformation, its deformation behavior, the response to the bainitic isothermal treatment, the appearance of yield point elongation and other peculiarities of plastic flow, and the mechanical properties of transformation-induced plasticity（TRIP） steel were tailored based on the chemical homogeneity and the relative distribution of the retained austenite, bainite, and ferrite in the microstructure. The presence of ferritic-pearlitic banded structure in the initial microstructure resulted in an inhomogeneous TRIP microstructure, in which the retained austenite and bainite were confined to some bands and it was found to be responsible for the resultant inferior mechanical properties. The appearance of discontinuous yielding for the chemically inhomogeneous material was related to the martensitic transformation of unstable retained austenite at the initial stage of tensile deformation. These results are essential for better understanding of the behavior of advanced high-strength steels and their applications.
基金financially supported by the National Natural Science Foundation of China (No. 51501031)the Natural Science Foundation of Liaoning Province (No. 20170520348)
文摘In the present study, a quenching treatment prior to two-stage heat treatment was conducted on a Fe-0.28C-1.55Mn-2.06Al transformation-induced plasticity steel to tailor the final microstructure. Compared with the microstructure of the ferrite, bainite and blocky retained austenite obtained by conventional two-stage heat treatment, the microstructure subjected to quenching plus two-stage heat treatment was composed of the ferrite, lath bainite and film-like retained austenite. The corresponding tensile behavior and mechanical stability of retained austenite were investigated by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. The results show that the mechanical stability of blocky retained austenite grains is lower and most of them transform to martensite during the tensile deformation, which leads to higher ultimate tensile strength and instantaneous work hardening exponent. Film-like retained austenite has relatively higher stability, which could cause sustained work hardening and high ductility as well as product of strength and elongation.
基金Item Sponsored by National Fundamental Project of Science and Technology of China(ZZ0113A0101)
文摘The effect of thermomechanical control processing（TMCP）on microstructure and mechanical properties of Fe-0.2C-1.44Si-1.32Mn hot rolled TRIP steel was investigated through experiments.Strain-induced transformation and transformation-induced plasticity behavior of retained austenite were analyzed.The results show that with multipass deformation,reduction per pass of more than critical deformation in austenite recrystallization region and total reduction of more than 58% in non-recrystallization region and high temperature section of two-phase region,austenite can be refined before γ→α transformation.It is beneficial to obtain refined ferrite grain in final microstructure.To obtain fine and uniform microstructure and excellent strength-ductility balance,a three-stage cooling process（laminar cooling-air cooling-ultra-fast cooling）after hot rolling was conducted.The ultimate tensile strength and elongation of the investigated steel can reach 663 MPa and 41%,respectively.