（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba...（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba（0.6）Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics were investigated. X-ray diffraction results indicated a pure cubic perovskite structure for all samples and that the lattice parameter increased till x=5 and then slightly decreased. A homogenous microstructure was observed with the addition of CaZrO3. Dielectric measurements revealed a relaxor-like characteristic for all samples and that the diffusivity γ reached the maximum value of 1.78 at x=5. With the addition of CaZrO3, the dielectric constant dependence on electric field was weakened, insulation resistivity enhanced and dielectric breakdown strength improved obviously and reached 19.9 k V/mm at x=7.5. In virtue of low dielectric loss（tan d〈0.001 5）, moderate dielectric constant（er 〉1 500） and high breakdown strength（Eb 〉17.5 k V/mm）, the CaZrO3 doped（Ba（0.6）Sr（0.4））0.85 Bi（0.1） TiO3 ceramic is a potential candidate material for high power electric applications.展开更多
In this research paper we are reporting synthesis, structural and optical investigations of barium strontium titanate borosilicate glasses with addition of La2O3. Glasses were synthesized by conventional rapid melt qu...In this research paper we are reporting synthesis, structural and optical investigations of barium strontium titanate borosilicate glasses with addition of La2O3. Glasses were synthesized by conventional rapid melt quench method. Infrared absorption spectra, for various (Ba,Sr)TiO3 borosilicate glass samples having glass system 64[(Ba1-xSrx)TiO3]-35[2SiO2-B2O3]-5[K2O]-1[La2O3] (x = 0.3, 0.5, 0.6, 0.8 and 1.0), were recorded over a continous spectral range from 450 - 4000 cm-1. IR spectra were analyzed to determine and differentiate the various vibrational modes in the structural changes. Raman spectroscopy of all glass samples were also carried out wavenumber range form 200 - 1500 cm-1. These two complementary spectroscopic techniques revealed that the network structure of the studied glasses is mainly based on BO3, pentaborate groups linked to BO4 tetrahedra and units placed in different structural groups, the BO3 units? are dominanting. The recorded IR and Raman spectra of different glasses are used to clarify the optical properties of the prepared glass samples correlating with their structure and compositions. UV-Vis spectroscopy was carried out in range of 200 - 800 nm. The optical band gap was found between 2.023 - 3.320 eV.展开更多
(Ba, Sr)RuO3 has been paid an attention as a promising electrode for (Ba, Sr)TiO3 dielectric material due to its similarity in structure and chemical composition with BST. In this study, (Ba, Sr)RuO3 conductive oxide ...(Ba, Sr)RuO3 has been paid an attention as a promising electrode for (Ba, Sr)TiO3 dielectric material due to its similarity in structure and chemical composition with BST. In this study, (Ba, Sr)RuO3 conductive oxide film was deposited on a 4 inch p-type Si wafer by metal organic chemical vapor deposition (MOCVD) using single cocktail source for the practical device application. Ba(TMHD)2, Sr(TMHD)2, Ru(TMHD)3 precursors and solvent [1-EtylePiPerdine (C7H15 N) ] as starting materials were mixed together for single cocktail source. A liquid delivery system (LDS) and a vaporization cell were utilized for the delivery and vaporization of single cocktail source, respectively. The source feeding rate was controlled by a liquid mass flow controller (LMFC). Deposition parameters, such as the oxygen flow and the source flow rate,were sensitive to phase formation, resistivity and the composition ratio of (Ba, Sr)RuO3 films. Highly (110)-textured (Ba,Sr)RuO3 film was obtained vhen the Ar/O2 ratio was 200/140 sccm at a source flow rate of 0.05 sccm. The process window of stoichiometric composition of BSR film was observed with varying the source flow rate from 0.05 sccm to 0.1 sccm.展开更多
基金Funded by the National Natural Science Foundation of China(No.51302093)the Fundamental Research Funds for the Central Universities of China(Nos.2014TS046,2015MS017)
文摘（Ba（0.6） Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics doped with x wt%CaZrO3（x= 0-10） were synthesized by solid-state reaction method. The effects of CaZrO3 amount on the dielectric properties and structure of（Ba（0.6）Sr（0.4））（0.85） Bi（0.1） TiO3 ceramics were investigated. X-ray diffraction results indicated a pure cubic perovskite structure for all samples and that the lattice parameter increased till x=5 and then slightly decreased. A homogenous microstructure was observed with the addition of CaZrO3. Dielectric measurements revealed a relaxor-like characteristic for all samples and that the diffusivity γ reached the maximum value of 1.78 at x=5. With the addition of CaZrO3, the dielectric constant dependence on electric field was weakened, insulation resistivity enhanced and dielectric breakdown strength improved obviously and reached 19.9 k V/mm at x=7.5. In virtue of low dielectric loss（tan d〈0.001 5）, moderate dielectric constant（er 〉1 500） and high breakdown strength（Eb 〉17.5 k V/mm）, the CaZrO3 doped（Ba（0.6）Sr（0.4））0.85 Bi（0.1） TiO3 ceramic is a potential candidate material for high power electric applications.
文摘In this research paper we are reporting synthesis, structural and optical investigations of barium strontium titanate borosilicate glasses with addition of La2O3. Glasses were synthesized by conventional rapid melt quench method. Infrared absorption spectra, for various (Ba,Sr)TiO3 borosilicate glass samples having glass system 64[(Ba1-xSrx)TiO3]-35[2SiO2-B2O3]-5[K2O]-1[La2O3] (x = 0.3, 0.5, 0.6, 0.8 and 1.0), were recorded over a continous spectral range from 450 - 4000 cm-1. IR spectra were analyzed to determine and differentiate the various vibrational modes in the structural changes. Raman spectroscopy of all glass samples were also carried out wavenumber range form 200 - 1500 cm-1. These two complementary spectroscopic techniques revealed that the network structure of the studied glasses is mainly based on BO3, pentaborate groups linked to BO4 tetrahedra and units placed in different structural groups, the BO3 units? are dominanting. The recorded IR and Raman spectra of different glasses are used to clarify the optical properties of the prepared glass samples correlating with their structure and compositions. UV-Vis spectroscopy was carried out in range of 200 - 800 nm. The optical band gap was found between 2.023 - 3.320 eV.
文摘(Ba, Sr)RuO3 has been paid an attention as a promising electrode for (Ba, Sr)TiO3 dielectric material due to its similarity in structure and chemical composition with BST. In this study, (Ba, Sr)RuO3 conductive oxide film was deposited on a 4 inch p-type Si wafer by metal organic chemical vapor deposition (MOCVD) using single cocktail source for the practical device application. Ba(TMHD)2, Sr(TMHD)2, Ru(TMHD)3 precursors and solvent [1-EtylePiPerdine (C7H15 N) ] as starting materials were mixed together for single cocktail source. A liquid delivery system (LDS) and a vaporization cell were utilized for the delivery and vaporization of single cocktail source, respectively. The source feeding rate was controlled by a liquid mass flow controller (LMFC). Deposition parameters, such as the oxygen flow and the source flow rate,were sensitive to phase formation, resistivity and the composition ratio of (Ba, Sr)RuO3 films. Highly (110)-textured (Ba,Sr)RuO3 film was obtained vhen the Ar/O2 ratio was 200/140 sccm at a source flow rate of 0.05 sccm. The process window of stoichiometric composition of BSR film was observed with varying the source flow rate from 0.05 sccm to 0.1 sccm.