Nano-Al2O3 particles modified Ag Cu Ni filler was adopted to braze the SiO2 ceramic and TC4.The effects of filler size as well as the brazing temperature on the interfacial microstructure and mechanical property of th...Nano-Al2O3 particles modified Ag Cu Ni filler was adopted to braze the SiO2 ceramic and TC4.The effects of filler size as well as the brazing temperature on the interfacial microstructure and mechanical property of the joints were investigated.Nanoscale filler reduced the phases dimension and promoted the homogeneous distribution of microstructure,obtaining a higher joint strength when compared to microscale filler.The increase of brazing temperature made the accelerating dissolution and diffusion of Ti,which promoted the increase of thickness of Ti4O7+TiSi2 layer adjacent to SiO2 ceramic and diffusion layer zone nearby TC4 alloy.The hypoeutectic structure was produced in the brazing seam due to the high Ti content.The maximum shear strength of^40 MPa was obtained at 950°C for 10 min.展开更多
基金supported by National Natural Science Foundation of China(Grant Nos.51505105,51875130 and 51775138)the Key Research&Development Program of Shandong Province(No.2017GGX40103).
文摘Nano-Al2O3 particles modified Ag Cu Ni filler was adopted to braze the SiO2 ceramic and TC4.The effects of filler size as well as the brazing temperature on the interfacial microstructure and mechanical property of the joints were investigated.Nanoscale filler reduced the phases dimension and promoted the homogeneous distribution of microstructure,obtaining a higher joint strength when compared to microscale filler.The increase of brazing temperature made the accelerating dissolution and diffusion of Ti,which promoted the increase of thickness of Ti4O7+TiSi2 layer adjacent to SiO2 ceramic and diffusion layer zone nearby TC4 alloy.The hypoeutectic structure was produced in the brazing seam due to the high Ti content.The maximum shear strength of^40 MPa was obtained at 950°C for 10 min.