A graphite carbon nitride(g-C3N4)modified Bi4O5I2 composite was successfully prepared insitu via the thermal treatment of a g-C3N4/Bi OI precursor at 400°C for 3 hr.The as-prepared g-C3N4/Bi4O5I2 showed high phot...A graphite carbon nitride(g-C3N4)modified Bi4O5I2 composite was successfully prepared insitu via the thermal treatment of a g-C3N4/Bi OI precursor at 400°C for 3 hr.The as-prepared g-C3N4/Bi4O5I2 showed high photocatalytic performance in Methyl Orange(MO)degradation under visible light.The best sample presented a degradation rate of 0.164 min^-1,which is 3.2 and 82 times as high as that of Bi4O5I2 and g-C3N4,respectively.The g-C3N4/Bi4O5I2 was characterized by X-ray powder diffractometer(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),Raman,X-ray photoelectron spectroscopy(XPS),ultraviolet-visible diffuse reflectance spectra(DRS),electrochemical impedance spectroscopy(EIS)and transient photocurrent response in order to explain the enhanced photoactivity.Results indicated that the decoration with a small amount of g-C3N4 influenced the specific surface area only slightly.Nevertheless,the capability for absorbing visible light was improved measurably,which was beneficial to the MO degradation.On top of that,a strong interaction between g-C3N4 and Bi4O5I2 was detected.This interplay promoted the formation of a favorable heterojunction structure and thereby enhanced the charge separation.Thus,the g-C3N4/Bi4O5I2 composite presented greater charge separation efficiency and much better photocatalytic performance than Bi4O5I2.Additionally,g-C3N4/Bi4O5I2 also presented high stability.·O2^- and holes were verified to be the main reactive species.展开更多
特征提取和健康状态的辨识是复杂系统健康状态评估中的关键问题。提出一种新的健康状态评估方法,该方法分为3个步骤:首先,采用经验模态分解(empirical model decomposition,EMD)和奇异值分解(singular value decomposition,SVD)来提取...特征提取和健康状态的辨识是复杂系统健康状态评估中的关键问题。提出一种新的健康状态评估方法,该方法分为3个步骤:首先,采用经验模态分解(empirical model decomposition,EMD)和奇异值分解(singular value decomposition,SVD)来提取振动信号的特征变量。然后,运用马田系统(Mahalanobis-Taguchi system,MTS)构造马氏空间,并对其进行优化,从而降低特征变量的维度。最后,提出了一种健康度(health index,HI)的概念,并且用来对复杂系统健康问题进行评估。该方法成功地应用在轴承的健康状态评估中。展开更多
基金financially supported by National Undergraduate Training Program for Innovation and Entrepreneurship(Nos.201810345012 and 201810345051)
文摘A graphite carbon nitride(g-C3N4)modified Bi4O5I2 composite was successfully prepared insitu via the thermal treatment of a g-C3N4/Bi OI precursor at 400°C for 3 hr.The as-prepared g-C3N4/Bi4O5I2 showed high photocatalytic performance in Methyl Orange(MO)degradation under visible light.The best sample presented a degradation rate of 0.164 min^-1,which is 3.2 and 82 times as high as that of Bi4O5I2 and g-C3N4,respectively.The g-C3N4/Bi4O5I2 was characterized by X-ray powder diffractometer(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),Raman,X-ray photoelectron spectroscopy(XPS),ultraviolet-visible diffuse reflectance spectra(DRS),electrochemical impedance spectroscopy(EIS)and transient photocurrent response in order to explain the enhanced photoactivity.Results indicated that the decoration with a small amount of g-C3N4 influenced the specific surface area only slightly.Nevertheless,the capability for absorbing visible light was improved measurably,which was beneficial to the MO degradation.On top of that,a strong interaction between g-C3N4 and Bi4O5I2 was detected.This interplay promoted the formation of a favorable heterojunction structure and thereby enhanced the charge separation.Thus,the g-C3N4/Bi4O5I2 composite presented greater charge separation efficiency and much better photocatalytic performance than Bi4O5I2.Additionally,g-C3N4/Bi4O5I2 also presented high stability.·O2^- and holes were verified to be the main reactive species.
文摘特征提取和健康状态的辨识是复杂系统健康状态评估中的关键问题。提出一种新的健康状态评估方法,该方法分为3个步骤:首先,采用经验模态分解(empirical model decomposition,EMD)和奇异值分解(singular value decomposition,SVD)来提取振动信号的特征变量。然后,运用马田系统(Mahalanobis-Taguchi system,MTS)构造马氏空间,并对其进行优化,从而降低特征变量的维度。最后,提出了一种健康度(health index,HI)的概念,并且用来对复杂系统健康问题进行评估。该方法成功地应用在轴承的健康状态评估中。