The influence of a longitudinal static magnetic field on microstructures and mechanical properties of Ni_(3)Al-based alloy during directional solidification at the growth speed of 25μm/s and 100μm/s has been experim...The influence of a longitudinal static magnetic field on microstructures and mechanical properties of Ni_(3)Al-based alloy during directional solidification at the growth speed of 25μm/s and 100μm/s has been experimentally investigated.Results reflected that the utilization of a 0.5 T magnetic field refines the Ni Al dendrites at both speeds of growth.When applying a high magnetic field,the columnar-to-equiaxed transition(CET)occurred at growth speed of 25μm/s and dendrite networks formed at growth speed of 100μm/s.Tensile property results indicated that the refinement of dendrites enhanced both plasticity and ultimate tensile strength of Ni-Al alloy.The change of microstructures and mechanical properties should be attributed to the combined action of the thermoelectric magnetic convection(TEMC)in mushy zone together with the thermoelectric magnetic force(TEMF)acting on the solid.When applying a low magnetic field(0.5 T),the TEMF is too small to fragment the dendrites,and the refined dendrites is mainly due to the TEMC in the interdendritic regions.At a lower growth speed,the TEMF is supposed to strong enough to fragment the dendrites and induce the occurrence of CET under 2 or 4 T.When the growth speed increased to 100μm/s,no obvious CET was observed,but a vertical secondary convection is induced by the circulation in the parallel plane,which promotes the growth of secondary and tertiary branches,leading to the formation of abnormally developed high order dendrites.The hierarchical dendritic structure was suggested to provide a channel for rapid crack propagation and thus degraded the mechanical properties.展开更多
In this paper, Ni-Cr-Al-Y-Si coating deposited by vacuum are deposition on the Ni_3Alalloy IC6, the typical use of which is for turbine blades and vanes, was examined.The results of the tests show that the tensile pro...In this paper, Ni-Cr-Al-Y-Si coating deposited by vacuum are deposition on the Ni_3Alalloy IC6, the typical use of which is for turbine blades and vanes, was examined.The results of the tests show that the tensile properties at room temperature and stress rupture properties at 1100℃ of the IC6 alloy were not obviously influenced by the coatings. At annealing state, limited element interdiffusion was observed. After stress rupture testing for 252 h at 1100℃/90 MPa, however,significant interdiffusion of Mo, Cr and Al took place between the coating layer and the substrate.The element diffustion did not result in the formation of brittle phases on the coating/substrate interface. No cracking and spallation in the coating were found.Therefore it can be concluded that the Ni-Cr-Al-Y-Si overlay coating was successful for protecting the IC6 alloy.展开更多
The microstructure,tensile properties at 20—950℃ and creep rupture properties at 700- 900℃ in a Ni_3Al-Fe based alloy after high temperature deformation have been studied.The results show the microstructure of the ...The microstructure,tensile properties at 20—950℃ and creep rupture properties at 700- 900℃ in a Ni_3Al-Fe based alloy after high temperature deformation have been studied.The results show the microstructure of the alloy is composed of γ′-and β-phases.The grain size and yield strength of the alloy is stable when the temperature≤600℃,and it is ductile at high temperature.The creep of the alloy at 700—900℃ is controlled by the climbing of dislo- cations,and the activation energy for creep is 439 KJ/mol with a stress exponent of 4.展开更多
基金supported by National Science and Technology Major Project“Aero engine and Gas Turbine”(2017-VII-00080102)National Key Research and Development Program of China(No.2019YFA0705300)+2 种基金National Nature Science Foundation of China(No.51701112 and No.51690162)Shanghai Rising-Star Program(20QA1403800 and 21QC1401500)Shanghai Science and Technology Committee(19DZ1100704)。
文摘The influence of a longitudinal static magnetic field on microstructures and mechanical properties of Ni_(3)Al-based alloy during directional solidification at the growth speed of 25μm/s and 100μm/s has been experimentally investigated.Results reflected that the utilization of a 0.5 T magnetic field refines the Ni Al dendrites at both speeds of growth.When applying a high magnetic field,the columnar-to-equiaxed transition(CET)occurred at growth speed of 25μm/s and dendrite networks formed at growth speed of 100μm/s.Tensile property results indicated that the refinement of dendrites enhanced both plasticity and ultimate tensile strength of Ni-Al alloy.The change of microstructures and mechanical properties should be attributed to the combined action of the thermoelectric magnetic convection(TEMC)in mushy zone together with the thermoelectric magnetic force(TEMF)acting on the solid.When applying a low magnetic field(0.5 T),the TEMF is too small to fragment the dendrites,and the refined dendrites is mainly due to the TEMC in the interdendritic regions.At a lower growth speed,the TEMF is supposed to strong enough to fragment the dendrites and induce the occurrence of CET under 2 or 4 T.When the growth speed increased to 100μm/s,no obvious CET was observed,but a vertical secondary convection is induced by the circulation in the parallel plane,which promotes the growth of secondary and tertiary branches,leading to the formation of abnormally developed high order dendrites.The hierarchical dendritic structure was suggested to provide a channel for rapid crack propagation and thus degraded the mechanical properties.
文摘In this paper, Ni-Cr-Al-Y-Si coating deposited by vacuum are deposition on the Ni_3Alalloy IC6, the typical use of which is for turbine blades and vanes, was examined.The results of the tests show that the tensile properties at room temperature and stress rupture properties at 1100℃ of the IC6 alloy were not obviously influenced by the coatings. At annealing state, limited element interdiffusion was observed. After stress rupture testing for 252 h at 1100℃/90 MPa, however,significant interdiffusion of Mo, Cr and Al took place between the coating layer and the substrate.The element diffustion did not result in the formation of brittle phases on the coating/substrate interface. No cracking and spallation in the coating were found.Therefore it can be concluded that the Ni-Cr-Al-Y-Si overlay coating was successful for protecting the IC6 alloy.
文摘The microstructure,tensile properties at 20—950℃ and creep rupture properties at 700- 900℃ in a Ni_3Al-Fe based alloy after high temperature deformation have been studied.The results show the microstructure of the alloy is composed of γ′-and β-phases.The grain size and yield strength of the alloy is stable when the temperature≤600℃,and it is ductile at high temperature.The creep of the alloy at 700—900℃ is controlled by the climbing of dislo- cations,and the activation energy for creep is 439 KJ/mol with a stress exponent of 4.