The microhardness curve trend and its relationships with microstructure and misorientation were analyzed to enhance the comprehension of the microstructure and mechanical property of micro-areas in Ti6 Al4 V laser-wel...The microhardness curve trend and its relationships with microstructure and misorientation were analyzed to enhance the comprehension of the microstructure and mechanical property of micro-areas in Ti6 Al4 V laser-welded joints with different welding speeds. The microhardness measured on the fusion line(H_m) is the highest from the weld center to the base metal. H_m increases with increasing weld width in a welded joint and increasing degree of the non-uniformity in all studied welded joints. The microhardness decreases from the weld metal to the base metal with decreasing amount of martensite α’ and increasing amount of original α phase. When the microstructure is mainly composed of martensite α’, the microhardness changes with the cooling rate, grain size of the martensite, and peak values of the fraction of misorientation angle of the martensite in a wide weld metal zone or weld center at different welding speeds, whereas the difference is small in a narrow weld metal zone.展开更多
The relation between the Mg treatment and ferrite grain boundaries misorientation was investigated. The orientation imaging microscopy technique based on electron backscattered diffraction technique （EBSD） was used ...The relation between the Mg treatment and ferrite grain boundaries misorientation was investigated. The orientation imaging microscopy technique based on electron backscattered diffraction technique （EBSD） was used in this work. （t was found that the addition of 0.005 wt% Mg to the steel could evidently increase the ratio of acicular ferrite crystals appearing at large angles boundaries to each other, which was attributed to the nucleation of the second-phase particles by the Mg treatment. The FBSD techniques provide a power- ful method to characterize and quantify the ferrite grain boundaries misorientation, in order to relate it to toughness.展开更多
Accumulative roll-bonding （ARB） was applied to Mg-Al-Zn magnesium alloy sheets to prepare ultrafine-grain microstructure. Significant grain refinement is achieved after three cycles of ARB with average grain size of...Accumulative roll-bonding （ARB） was applied to Mg-Al-Zn magnesium alloy sheets to prepare ultrafine-grain microstructure. Significant grain refinement is achieved after three cycles of ARB with average grain size of about 1.3 μm. The microstructure is characterized by nearly uniform ultrafine equiaxed microstructure without twins. The evolution of the misorientation distribution during ARB was measured by EBSD. Grain refinement can be contributed to the grain subdivision induced by severe accumulated strain, the accumulated strain enhanced concurrent dynamic recovery and recrystallization as well as the complicated distribution of interface and shear strain during ARB.展开更多
As an advanced solid state bonding process,plastic deformation bonding(PDB)is a highly reliable metallurgical joining method that produces significant plastic deformation at the bonding interface of welded joints thro...As an advanced solid state bonding process,plastic deformation bonding(PDB)is a highly reliable metallurgical joining method that produces significant plastic deformation at the bonding interface of welded joints through thermo-mechanical coupling.In this study,PDB behavior of IN718 superalloy was systematically investigated by performing a series of isothermal compression tests at various processing conditions.It was revealed that new grains evolved in the bonding area through discontinuous dynamic recrystallization(DDRX)at 1000–1150℃.Electron backscattered diffraction(EBSD)and transmission electron microscopy(TEM)results revealed that the bonding of joints is related with interfacial grain boundary(IGB)bulging process,which is considered as a nucleation process of DRXed grain under different deformation environments.During recrystallization process,the bonded interface moved due to strain-induced boundary migration(SIBM)process.Stored energy difference(caused by accumulation of dislocations at the bonding interface)was the dominant factor for SIBM during DRX.The mechanical properties of the bonded joints were dependent upon the recrystallized microstructure and SIBM ensued during PDB.展开更多
The evolution of the microstructure, texture, and microhardness of 5754 aluminum alloy subjected to high-temperature plastic deformation under different deformation conditions was studied on the basis of thermal simul...The evolution of the microstructure, texture, and microhardness of 5754 aluminum alloy subjected to high-temperature plastic deformation under different deformation conditions was studied on the basis of thermal simulations and electron-backscattered diffraction and Vickers microhardness experiments. The results of a misorientation angle study show that an increase in the deformation temperature and strain rate promoted the transformation of low-angle grain boundaries to high-angle grain boundaries, which contributed to dynamic recrystallization. The effect of the deformation parameters on the texture and its evolution during the recrystallization process was explored on the basis of the orientation distribution function. The results demonstrate that the deformed samples mainly exhibited the features of type A, B, and B textures. The formation and growth of the recrystallized grains clearly affected the texture evolution. The microhardness results show that the variation of the microhardness was closely related to the temperature, strain rate, and dynamic recrystallization.展开更多
基金Project(51875442)supported by the National Natural Science Foundation of China。
文摘The microhardness curve trend and its relationships with microstructure and misorientation were analyzed to enhance the comprehension of the microstructure and mechanical property of micro-areas in Ti6 Al4 V laser-welded joints with different welding speeds. The microhardness measured on the fusion line(H_m) is the highest from the weld center to the base metal. H_m increases with increasing weld width in a welded joint and increasing degree of the non-uniformity in all studied welded joints. The microhardness decreases from the weld metal to the base metal with decreasing amount of martensite α’ and increasing amount of original α phase. When the microstructure is mainly composed of martensite α’, the microhardness changes with the cooling rate, grain size of the martensite, and peak values of the fraction of misorientation angle of the martensite in a wide weld metal zone or weld center at different welding speeds, whereas the difference is small in a narrow weld metal zone.
文摘The relation between the Mg treatment and ferrite grain boundaries misorientation was investigated. The orientation imaging microscopy technique based on electron backscattered diffraction technique （EBSD） was used in this work. （t was found that the addition of 0.005 wt% Mg to the steel could evidently increase the ratio of acicular ferrite crystals appearing at large angles boundaries to each other, which was attributed to the nucleation of the second-phase particles by the Mg treatment. The FBSD techniques provide a power- ful method to characterize and quantify the ferrite grain boundaries misorientation, in order to relate it to toughness.
基金Project (50801027) supported by the National Natural Science Foundation of ChinaProject(2007001) supported by the Public Foundation of Guangdong Key Laboratory for Advanced Metallic Materials Processing,South China University of Technology,China
文摘Accumulative roll-bonding （ARB） was applied to Mg-Al-Zn magnesium alloy sheets to prepare ultrafine-grain microstructure. Significant grain refinement is achieved after three cycles of ARB with average grain size of about 1.3 μm. The microstructure is characterized by nearly uniform ultrafine equiaxed microstructure without twins. The evolution of the misorientation distribution during ARB was measured by EBSD. Grain refinement can be contributed to the grain subdivision induced by severe accumulated strain, the accumulated strain enhanced concurrent dynamic recovery and recrystallization as well as the complicated distribution of interface and shear strain during ARB.
基金the National Key Research and Development Program[grant number 2018YFA0702900]the National Natural Science Foundation of China[grant numbers U1508215,51774265]+2 种基金the National Science and Technology Major Project of China[Grant No.2019ZX06004010]the Key Program of the Chinese Academy of Sciences[Grant No.ZDRW-CN-2017-1]the CAS Interdisciplinary Innovation Team。
文摘As an advanced solid state bonding process,plastic deformation bonding(PDB)is a highly reliable metallurgical joining method that produces significant plastic deformation at the bonding interface of welded joints through thermo-mechanical coupling.In this study,PDB behavior of IN718 superalloy was systematically investigated by performing a series of isothermal compression tests at various processing conditions.It was revealed that new grains evolved in the bonding area through discontinuous dynamic recrystallization(DDRX)at 1000–1150℃.Electron backscattered diffraction(EBSD)and transmission electron microscopy(TEM)results revealed that the bonding of joints is related with interfacial grain boundary(IGB)bulging process,which is considered as a nucleation process of DRXed grain under different deformation environments.During recrystallization process,the bonded interface moved due to strain-induced boundary migration(SIBM)process.Stored energy difference(caused by accumulation of dislocations at the bonding interface)was the dominant factor for SIBM during DRX.The mechanical properties of the bonded joints were dependent upon the recrystallized microstructure and SIBM ensued during PDB.
基金financial support from the Natural Science Foundation of China (No. 51275533)the State Key Laboratory of High-Performance Complex Manufacturing (No. zzyjkt2013-10B),Central South University, Chinathe portion provided by the Academician Workstation Foundation of Yinhai Aluminum Industry Co., Ltd., Liuzhou, China
文摘The evolution of the microstructure, texture, and microhardness of 5754 aluminum alloy subjected to high-temperature plastic deformation under different deformation conditions was studied on the basis of thermal simulations and electron-backscattered diffraction and Vickers microhardness experiments. The results of a misorientation angle study show that an increase in the deformation temperature and strain rate promoted the transformation of low-angle grain boundaries to high-angle grain boundaries, which contributed to dynamic recrystallization. The effect of the deformation parameters on the texture and its evolution during the recrystallization process was explored on the basis of the orientation distribution function. The results demonstrate that the deformed samples mainly exhibited the features of type A, B, and B textures. The formation and growth of the recrystallized grains clearly affected the texture evolution. The microhardness results show that the variation of the microhardness was closely related to the temperature, strain rate, and dynamic recrystallization.