Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stre...Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stress is -54 MPa. The strains of debonding initiation of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing are 2.6%, 5.1% and 8.6%, respectively, and the average radii of the debonding patches with debonding initiation are 27.5, 17.1 and 19.4 μm, respectively. The true critical debonding stresses of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing can be estimated as 220.4, 394.5 and 627.9 MPa, respectively. Interfacial shear lag model is modified and polynomial fitting equation of the interfacial shear strength of TiO2 nanotube film is demonstrated under debonding conditions. The modification and polynomial fitting are reliable since good agreement of the interfacial shear strengths after fitting is obtained compared with those results from the crack density analysis.展开更多
The analysis of the dynamic stress on the particle-matrix interface in particle-reinforced composite for the reason that this stress may lead to the microvoids' nucleation due to the interfacial debonding were stu...The analysis of the dynamic stress on the particle-matrix interface in particle-reinforced composite for the reason that this stress may lead to the microvoids' nucleation due to the interfacial debonding were studied. For simplification, a sphere containing a concentric rigid spherical particle was taken as the representative volume element (RVE). The Laplace transformation was used to derive the basic equations, and the analytical solutions were obtained by means of Hankel transformation. Moreover, the influences of the inertia and viscosity on the debonding damage were also discussed.展开更多
基金Project (51274248) supported by the National Natural Science Foundation of ChinaProject (20110946Z) supported by the State Key Laboratory of Powder Metallurgy, China
文摘Curvature method was used to measure the residual stress and substrate straining tensile test was carried out to study the debonding behavior of TiO2 nanotube film. The results indicate that the internal residual stress is -54 MPa. The strains of debonding initiation of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing are 2.6%, 5.1% and 8.6%, respectively, and the average radii of the debonding patches with debonding initiation are 27.5, 17.1 and 19.4 μm, respectively. The true critical debonding stresses of TiO2 nanotube films without annealing, with 250 °C annealing and with 400 °C annealing can be estimated as 220.4, 394.5 and 627.9 MPa, respectively. Interfacial shear lag model is modified and polynomial fitting equation of the interfacial shear strength of TiO2 nanotube film is demonstrated under debonding conditions. The modification and polynomial fitting are reliable since good agreement of the interfacial shear strengths after fitting is obtained compared with those results from the crack density analysis.
文摘The analysis of the dynamic stress on the particle-matrix interface in particle-reinforced composite for the reason that this stress may lead to the microvoids' nucleation due to the interfacial debonding were studied. For simplification, a sphere containing a concentric rigid spherical particle was taken as the representative volume element (RVE). The Laplace transformation was used to derive the basic equations, and the analytical solutions were obtained by means of Hankel transformation. Moreover, the influences of the inertia and viscosity on the debonding damage were also discussed.