Pt3Co alloy nanoparticles were prepared by the reduction of H2PtCl6 and Co(OOCCH3)2 using NaBH4 as a reducing agent. The Pt3Co core-Pt shell nanoparticles (Pt3Co@Pt) were synthesized using hydrogen absorption reductio...Pt3Co alloy nanoparticles were prepared by the reduction of H2PtCl6 and Co(OOCCH3)2 using NaBH4 as a reducing agent. The Pt3Co core-Pt shell nanoparticles (Pt3Co@Pt) were synthesized using hydrogen absorption reduction and characterized by plasma-atomic emission spectrometry (ICP), transmission electron microscopy (TEM), X-ray diffraction (XRD) and SQUID magnetometer. The results show that average size of Pt3Co@Pt nanoparticles is 3.6 nm with a standard deviation of 0.9 nm. Heating Pt3Co nanoparticles in air at 700 ℃ for 1 h, Co in Pt3Co nanoparticles was oxidized to Co3O4 and CoO; while no oxidation tendency was detected for Pt3Co@Pt nanoparticles. The crystallize structure of Pt3Co@Pt changed from the face centered cube (fcc) to the face centered tetragonal (fct) after the heating treatment. The coercivity of the heated Pt3Co@Pt reached to 276 Oe at room temperature.展开更多
基金National Natural Science Foundation of China(20833002,20903057,51172110)Research Fund for the Doctoral Program of Higher Education of China(20093223120002)+2 种基金Natural Science Foundation of Jiangsu Province(BK2010525,BK2011750)Foundation of Jiangsu Educational Committee(09KJB150007,08KJB150011)Scientific Research Foundation of Nanjing University of Posts and Telecommunications(NY208046,NY208025,NY208026)~~
文摘Pt3Co alloy nanoparticles were prepared by the reduction of H2PtCl6 and Co(OOCCH3)2 using NaBH4 as a reducing agent. The Pt3Co core-Pt shell nanoparticles (Pt3Co@Pt) were synthesized using hydrogen absorption reduction and characterized by plasma-atomic emission spectrometry (ICP), transmission electron microscopy (TEM), X-ray diffraction (XRD) and SQUID magnetometer. The results show that average size of Pt3Co@Pt nanoparticles is 3.6 nm with a standard deviation of 0.9 nm. Heating Pt3Co nanoparticles in air at 700 ℃ for 1 h, Co in Pt3Co nanoparticles was oxidized to Co3O4 and CoO; while no oxidation tendency was detected for Pt3Co@Pt nanoparticles. The crystallize structure of Pt3Co@Pt changed from the face centered cube (fcc) to the face centered tetragonal (fct) after the heating treatment. The coercivity of the heated Pt3Co@Pt reached to 276 Oe at room temperature.