The effects of B2O3 addition on both the sintering behavior and microwave dielectric properties of CaO-B2O3-SiO2 （CBS） glass ceramics were investigated by Fourier transform infrared spectroscopy （FTIR）, X-ray diff...The effects of B2O3 addition on both the sintering behavior and microwave dielectric properties of CaO-B2O3-SiO2 （CBS） glass ceramics were investigated by Fourier transform infrared spectroscopy （FTIR）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. The results show that the increasing amount of B203 causes the increase of the contents of [BO3], [BO4] and [SiO4], which deduces the increase of CaB204 and a-SiO2 and the decrease of CaSiO3 correspondingly. No new phase is observed throughout the entire experiments. A bulk density of 2.54 g/cm3, a thermal expansion coefficient value of 11.95× 10-6 ℃-1 （20-500℃）, a dielectric constant er value of 6.42 and a dielectric loss tanδ value of 0.000 9 （measured at 9.7 GHz） are obtained for CBS glass ceramics containing 35%-B203 （mass fraction） sintered at 850 ℃ for 15 min.展开更多
CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning ...CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.展开更多
ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient t...ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.展开更多
基金Project(2007AA03Z0455) supported by the National High-Technology Research and Development Program of ChinaProject(BE2009168) supported by the Natural Science Foundation of Jiangsu Province in ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institution,China
文摘The effects of B2O3 addition on both the sintering behavior and microwave dielectric properties of CaO-B2O3-SiO2 （CBS） glass ceramics were investigated by Fourier transform infrared spectroscopy （FTIR）, X-ray diffractometry （XRD） and scanning electron microscopy （SEM）. The results show that the increasing amount of B203 causes the increase of the contents of [BO3], [BO4] and [SiO4], which deduces the increase of CaB204 and a-SiO2 and the decrease of CaSiO3 correspondingly. No new phase is observed throughout the entire experiments. A bulk density of 2.54 g/cm3, a thermal expansion coefficient value of 11.95× 10-6 ℃-1 （20-500℃）, a dielectric constant er value of 6.42 and a dielectric loss tanδ value of 0.000 9 （measured at 9.7 GHz） are obtained for CBS glass ceramics containing 35%-B203 （mass fraction） sintered at 850 ℃ for 15 min.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject(BE2010194) supported by Science&Technology Pillar Program of Jiangsu Province, China+1 种基金Project(KF201103) supported by the State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, ChinaProject supported by the Priority Academic Development of Jiangsu Higher Education Institutions, China
文摘CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.
基金Funded by the Shanghai Leading Academic Discipline Project (B502)Shanghai Key Laboratory Project (08DZ2230500)
文摘ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.