The formation characteristics of calcium aluminates in the CaO-Al2O3-SiO2 system with sodium oxide was investigated by XRD, SEM-EDS and DSC-TG technologies. The main phases in the clinker after sintering at 1350 °...The formation characteristics of calcium aluminates in the CaO-Al2O3-SiO2 system with sodium oxide was investigated by XRD, SEM-EDS and DSC-TG technologies. The main phases in the clinker after sintering at 1350 °C are 12CaO?7Al2O3, 2CaO?Al2O3?SiO2 and 2CaO?SiO2 when the mass ratio of Al2O3 to SiO2 is 3.0 and the molar ratio of CaO to Al2O3 is 1.0. The proportion of 12CaO?7Al2O3 increases with the increase of Na2O addition when the molar ratio of Na2O to Al2O3 is from 0 to 0.4, while the proportion of 2CaO?Al2O3?SiO2 decreases with the increase of Na2O addition. Na2O forms solid solution in 12CaO?7Al2O3, which increases the volume of elementary cell of 12CaO?7Al2O3. The formation temperature of 12CaO?7Al2O3 is decreased by 30 °C when the molar ratio of Na2O to Al2O3 increases from 0 to 0.4 determined by DSC. The alumina leaching property of clinker increases obviously with the increase of Na2O addition.展开更多
The effects of Fe2O3 content on the microstructure and mechanical properties of the CaO-Al2O3-SiO2 system were investigated by differential thermal analysis（DTA）, X-ray diffraction（XRD）, scanning electron microsc...The effects of Fe2O3 content on the microstructure and mechanical properties of the CaO-Al2O3-SiO2 system were investigated by differential thermal analysis（DTA）, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, electron spin resonance（ESR）, and Mssbauer spectroscopy. The results show that the addition of Fe2O3 does not affect the main crystalline phase in the prepared glasses, but it reduces the crystallisation peak temperature, increases the crystallisation activation energy, and reduces the crystal granularity. The ESR results indicate that Fe2O3 can promote crystallization, as it leads to the phase separation of the CaO-Al2O3-SiO2 system due to axial distortion. Moreover, Fe2O3 alters the network structure of the CaO-Al2O3-SiO2 system, allowing Fe3＋ to enter octahedral sites that exhibit higher symmetry than tetrahedral sites. All of these factors are favourable to increasing the bending strength. The Mssbauer results reveal that there are two types of coordination for both Fe3＋ and Fe2＋ and the bending strength of the CaO-Al2O3-SiO2 system increases with the amount of six-coordinate Fe3＋. The increasing interaction between Fe3＋ and Fe2＋ can also enhance the bending strength of the CaO-Al2O3-SiO2 system. The microhardness of the CaO-Al2O3-SiO2 system was determined to be HV 896.9 and the bending strength to be 217 MPa under the heat treatment conditions of nucleation temperature of 700 °C and nucleation time of 2 h, crystallization temperature of 910 °C and crystallization time of 3 h.展开更多
Gold tailings glass-ceramics of CaO-MgO-Al2O3-SiO2 system have been studied by usinggold tailings as a major raw materials, its main crystalline phase is diopside. The effect of gold tailings amounts added into the ba...Gold tailings glass-ceramics of CaO-MgO-Al2O3-SiO2 system have been studied by usinggold tailings as a major raw materials, its main crystalline phase is diopside. The effect of gold tailings amounts added into the base glass on the crystallization behavior have beeninvestigated by means of DTA, SEM, EDAX and XRD. The experimental results showthat the crystallization peak temperature decreases and volumecrystallization can be enhancedwith increasing the amounts of gold tailings from 40 to 70 wt%. It is the sulfide included ingold tailings that promote .the base glass to nueleate internally. This diopside glassceramicscan be employed as building decorative materials.展开更多
The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specro...The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.展开更多
基金Projects(51174054,51104041)supported by the National Natural Science Foundation of China
文摘The formation characteristics of calcium aluminates in the CaO-Al2O3-SiO2 system with sodium oxide was investigated by XRD, SEM-EDS and DSC-TG technologies. The main phases in the clinker after sintering at 1350 °C are 12CaO?7Al2O3, 2CaO?Al2O3?SiO2 and 2CaO?SiO2 when the mass ratio of Al2O3 to SiO2 is 3.0 and the molar ratio of CaO to Al2O3 is 1.0. The proportion of 12CaO?7Al2O3 increases with the increase of Na2O addition when the molar ratio of Na2O to Al2O3 is from 0 to 0.4, while the proportion of 2CaO?Al2O3?SiO2 decreases with the increase of Na2O addition. Na2O forms solid solution in 12CaO?7Al2O3, which increases the volume of elementary cell of 12CaO?7Al2O3. The formation temperature of 12CaO?7Al2O3 is decreased by 30 °C when the molar ratio of Na2O to Al2O3 increases from 0 to 0.4 determined by DSC. The alumina leaching property of clinker increases obviously with the increase of Na2O addition.
基金Project(50974090)supported by the National Natural Science Foundation of ChinaProjects(JCYJ20140418182819155,JCYJ20130329113849606)supported by the Shenzhen Dedicated Funding of Strategic Emerging Industry Development Program,China
文摘The effects of Fe2O3 content on the microstructure and mechanical properties of the CaO-Al2O3-SiO2 system were investigated by differential thermal analysis（DTA）, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, electron spin resonance（ESR）, and Mssbauer spectroscopy. The results show that the addition of Fe2O3 does not affect the main crystalline phase in the prepared glasses, but it reduces the crystallisation peak temperature, increases the crystallisation activation energy, and reduces the crystal granularity. The ESR results indicate that Fe2O3 can promote crystallization, as it leads to the phase separation of the CaO-Al2O3-SiO2 system due to axial distortion. Moreover, Fe2O3 alters the network structure of the CaO-Al2O3-SiO2 system, allowing Fe3＋ to enter octahedral sites that exhibit higher symmetry than tetrahedral sites. All of these factors are favourable to increasing the bending strength. The Mssbauer results reveal that there are two types of coordination for both Fe3＋ and Fe2＋ and the bending strength of the CaO-Al2O3-SiO2 system increases with the amount of six-coordinate Fe3＋. The increasing interaction between Fe3＋ and Fe2＋ can also enhance the bending strength of the CaO-Al2O3-SiO2 system. The microhardness of the CaO-Al2O3-SiO2 system was determined to be HV 896.9 and the bending strength to be 217 MPa under the heat treatment conditions of nucleation temperature of 700 °C and nucleation time of 2 h, crystallization temperature of 910 °C and crystallization time of 3 h.
文摘Gold tailings glass-ceramics of CaO-MgO-Al2O3-SiO2 system have been studied by usinggold tailings as a major raw materials, its main crystalline phase is diopside. The effect of gold tailings amounts added into the base glass on the crystallization behavior have beeninvestigated by means of DTA, SEM, EDAX and XRD. The experimental results showthat the crystallization peak temperature decreases and volumecrystallization can be enhancedwith increasing the amounts of gold tailings from 40 to 70 wt%. It is the sulfide included ingold tailings that promote .the base glass to nueleate internally. This diopside glassceramicscan be employed as building decorative materials.
文摘The effect of Cr2O3 on the nucleation and crystallization of Na2O-CaO-Al2O3-SiO2-F- glass has been investigated by means of ESR(Electron Spin Resonance), SEM(Scanning Electron Microscope), EDS(Energy Dispersive Specrometer) and so on. Computer pattern recognition is applied to optimize the heat-treatment schedules. The experimental results show that the base glass containing more than 1 .5 % (mass fraction) Cr2O3 can be nucleated internally and converted to spheroidal crystal glass materials. The spheroidal crystal consisted of fibrous wollastonite crystals radiating from a center. The residual glass phase filled in the interstices between the fibers and between the spherulites. During heat treatment process, the valence states ofchromium changed from Cr6- to Cr3-, and the Cr-spinel solidsolution [CaCr2O4] precipitated followed this valence change. At the primary stage of crystallization, the Cr-spinel could act as a nucleating center on which the principal or}stalline phase β-CaSiO3 grew epitaxially.