The effects of Ni content（0–2.1wt%）on the cast and solid-solution microstructures of Cu-0.4wt%Be alloys were investigated,and the corresponding mechanisms of influence were analyzed.The results show that the amount...The effects of Ni content（0–2.1wt%）on the cast and solid-solution microstructures of Cu-0.4wt%Be alloys were investigated,and the corresponding mechanisms of influence were analyzed.The results show that the amount of precipitated phase increases in the cast alloys with increasing Ni content.When the Ni content is 0.45wt%or 0.98wt%,needle-like Be_（21）Ni_5 phases form in the grains and are mainly distributed in the interdendritic regions.When the Ni content is 1.5wt%or greater,a large number of needle-like precipitates form in the grains and chain-like Be_（21）Ni_5 and Be Ni precipitates form along the grain boundaries.The addition of Ni can substantially refine the cast and solid-solution microstructures of Cu-0.4wt%Be alloys.The hindering effects of both the dissolution of Ni into the matrix and the formation of Be–Ni precipitates on grain-boundary migration are mainly responsible for refining the cast and solid-solution microstructures of Cu-0.4wt%Be alloys.Higher Ni contents result in finer microstructures;however,given the precipitation characteristics of Be–Ni phases and their dissolution into the matrix during the solid-solution treatment,the upper limit of the Ni content is 1.5wt%–2.1wt%.展开更多
The effects of an applied magnetic field on the corrosion process of beryllium copper in NaCl solution have been investigated by electrochemical measurements, scanning electron microscopy （SEM） and energy dispersive...The effects of an applied magnetic field on the corrosion process of beryllium copper in NaCl solution have been investigated by electrochemical measurements, scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS）. The results showed that a horizontal magnetic field with 0.4 T barely shifted the open circuit potentials （Ecorr） of beryllium copper in NaCl solution with different concentrations. However, the horizontal magnetic field increased the limiting current density of beryllium copper in NaCl solution with low concentration, while decreased the limiting current density of beryllium copper in NaCl solution with high concentration. It was found that magnetic field accelerated the diffusion of CuCl2- away from the electrode surface and delayed the formation of Cu2O. The results of SEM and EDS showed that the inffuence of magnetic field over the elements distribution of the corrosion products differed from the different concentration of the immersion solution.展开更多
基金financially supported by the National Key Research and Development Program of China (No.2016YFB0301300)
文摘The effects of Ni content（0–2.1wt%）on the cast and solid-solution microstructures of Cu-0.4wt%Be alloys were investigated,and the corresponding mechanisms of influence were analyzed.The results show that the amount of precipitated phase increases in the cast alloys with increasing Ni content.When the Ni content is 0.45wt%or 0.98wt%,needle-like Be_（21）Ni_5 phases form in the grains and are mainly distributed in the interdendritic regions.When the Ni content is 1.5wt%or greater,a large number of needle-like precipitates form in the grains and chain-like Be_（21）Ni_5 and Be Ni precipitates form along the grain boundaries.The addition of Ni can substantially refine the cast and solid-solution microstructures of Cu-0.4wt%Be alloys.The hindering effects of both the dissolution of Ni into the matrix and the formation of Be–Ni precipitates on grain-boundary migration are mainly responsible for refining the cast and solid-solution microstructures of Cu-0.4wt%Be alloys.Higher Ni contents result in finer microstructures;however,given the precipitation characteristics of Be–Ni phases and their dissolution into the matrix during the solid-solution treatment,the upper limit of the Ni content is 1.5wt%–2.1wt%.
基金supported by the National Natural Science Foundation of China (No. 50771020)
文摘The effects of an applied magnetic field on the corrosion process of beryllium copper in NaCl solution have been investigated by electrochemical measurements, scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS）. The results showed that a horizontal magnetic field with 0.4 T barely shifted the open circuit potentials （Ecorr） of beryllium copper in NaCl solution with different concentrations. However, the horizontal magnetic field increased the limiting current density of beryllium copper in NaCl solution with low concentration, while decreased the limiting current density of beryllium copper in NaCl solution with high concentration. It was found that magnetic field accelerated the diffusion of CuCl2- away from the electrode surface and delayed the formation of Cu2O. The results of SEM and EDS showed that the inffuence of magnetic field over the elements distribution of the corrosion products differed from the different concentration of the immersion solution.