制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶...制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶化2h后能够获得较理想的磁铁矿主晶相和硅灰石次晶相均匀致密分布的微观组织,所得微晶玻璃具有最佳的磁性能.铁含量提高能够增加微晶玻璃的磁性,然而会抑制微晶玻璃表面羟基磷灰石的形成,从而降低其生物活性.展开更多
The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The co...The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The corresponding physical properties of 37. 91% CAO-43.09% SiO2-5% Al2O3-5% MgO-2% Li20-7% B2O3 mould fluxes were as follows： the melting point was 909℃, the flowing temperature was 1 160℃, the viscosity and surface tension at 1300 ℃ were 0. 4 Pa · s and 0.32 N/m respectively, which could meet the demands for certain kinds of steels for mould fluxes in continuous casting.展开更多
文摘制备了添加少量B2O3和P2O5后的Fe2O3 CaO SiO2体系铁磁微晶玻璃,并进行了微观结构分析、XRD分析、磁性检测以及生理模拟液的浸泡实验.实验结果表明,制备的微晶玻璃材料同时具备磁性和生物活性这两种重要性能.不经过核化处理在1000℃晶化2h后能够获得较理想的磁铁矿主晶相和硅灰石次晶相均匀致密分布的微观组织,所得微晶玻璃具有最佳的磁性能.铁含量提高能够增加微晶玻璃的磁性,然而会抑制微晶玻璃表面羟基磷灰石的形成,从而降低其生物活性.
基金Item Sponsored by National Natural Science Foundation of China (50474037) Jiangsu Province Natural Science Foundation forUniversity of China (04BJK430022)
文摘The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The corresponding physical properties of 37. 91% CAO-43.09% SiO2-5% Al2O3-5% MgO-2% Li20-7% B2O3 mould fluxes were as follows： the melting point was 909℃, the flowing temperature was 1 160℃, the viscosity and surface tension at 1300 ℃ were 0. 4 Pa · s and 0.32 N/m respectively, which could meet the demands for certain kinds of steels for mould fluxes in continuous casting.