Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on...Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.展开更多
基金973 Program (2006CB202500)the National Natural Science Foundation of China (20676096)New Century Excellent Talents in University.9gram (2006CB202500)
文摘Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.
基金Jointly Funded Project(61179055)of Chinese Civil Aviation AuthorityNational Natural Science Foundation of China+1 种基金Major State Basic Research Development Program(2014CB921300)Talent Grant(5030450104)of Educational Commission of Guangdong Province,China