LiNi0.8Co0.1Mn0.1O2 cathode was synthesized using transition metal acetates under different synthesis conditions. Simultaneous thermogravimetric–differential scanning calorimetry–derivative thermogravimetric analysi...LiNi0.8Co0.1Mn0.1O2 cathode was synthesized using transition metal acetates under different synthesis conditions. Simultaneous thermogravimetric–differential scanning calorimetry–derivative thermogravimetric analysis was applied to investigating the mixture of transition metal acetates. X-ray powder diffraction and charge–discharge test were adopted to characterize the as-prepared LiNi0.8Co0.1Mn0.1O2. The mixture of transition metal acetates undergoes dehydration and decomposition during heating. All the examined LiNi0.8Co0.1Mn0.1O2 samples have a layered structure with R3 m space group. LiNi0.8Co0.1Mn0.1O2 samples prepared with different lithium sources under different synthesis conditions exhibit very different charge–discharge performances. The sample synthesized via the procedure of sintering at 800 °C after heating lithium carbonate and transition metal acetates at 550 °C achieves a highest capacity of 200.8 m A·h/g and an average capacity of 188.1 mA ·h/g in the first 20 cycles at 0.2C.展开更多
基金Project(2010ZC051)supported by the Natural Science Foundation of Yunnan Province,ChinaProject(20140439)supported by the Analysis and Testing Foundation from Kunming University of Science and Technology,ChinaProject(14118245)supported by the Starting Research Fund from Kunming University of Science and Technology,China
文摘LiNi0.8Co0.1Mn0.1O2 cathode was synthesized using transition metal acetates under different synthesis conditions. Simultaneous thermogravimetric–differential scanning calorimetry–derivative thermogravimetric analysis was applied to investigating the mixture of transition metal acetates. X-ray powder diffraction and charge–discharge test were adopted to characterize the as-prepared LiNi0.8Co0.1Mn0.1O2. The mixture of transition metal acetates undergoes dehydration and decomposition during heating. All the examined LiNi0.8Co0.1Mn0.1O2 samples have a layered structure with R3 m space group. LiNi0.8Co0.1Mn0.1O2 samples prepared with different lithium sources under different synthesis conditions exhibit very different charge–discharge performances. The sample synthesized via the procedure of sintering at 800 °C after heating lithium carbonate and transition metal acetates at 550 °C achieves a highest capacity of 200.8 m A·h/g and an average capacity of 188.1 mA ·h/g in the first 20 cycles at 0.2C.