Plasma arc welding was used to join SiCp/Al composite with titanium as alloying filler material. Microstructure of the weld was characterized by an optical microscope. The results show that the harmful needle-like pha...Plasma arc welding was used to join SiCp/Al composite with titanium as alloying filler material. Microstructure of the weld was characterized by an optical microscope. The results show that the harmful needle-like phase Al4C3 is completely eliminated in the weld of SiCp/Al metal matrix composite(MMC) by in-situ weld-alloying/plasma arc welding with titanium as the alloying element. The wetting property between reinforced phase and Al matrix is improved, a stable weld puddle is gotten and a novel composite-material welded joint reinforced by TiN, AlN and TiC is produced. And the tensile-strength and malleability of the welded joints are improved effectively because of the use of titanium.展开更多
The formation process, microstructure and mechanical properties of transient liquid phase (TLP) bonded aluminium based metal matrix composite (MMC) joint with copper interlayer were investigated. The formation process...The formation process, microstructure and mechanical properties of transient liquid phase (TLP) bonded aluminium based metal matrix composite (MMC) joint with copper interlayer were investigated. The formation process of the TLP joint comprises a number of stages: plastic deformation and solid diffusion (stage 1), dissolution of interlayer and base metal (stage 2), isothermal solidification (stage 3) and homogenization (stage 4). The microstructure of the joint depends on the joint formation process (distinct stages). The plastic deformation and solid diffusion in stage 1 favoure the intimate contact at interfaces and liquid layer formation. The microstructure of joint consists of aluminium solid solution, alumina particle, Al 2Cu and MgAl 2O 4 compounds in stage 2. The most pronounced feature of joint microstructure in stage 3 is the alumina particle segregation in the center of the joint. The increase of joint shear strength with increasing bonding temperature is mainly attributed to improving the fluidity and wettability of liquid phase and decreasing the amount of Al 2Cu brittle phase in the joint. The principal reason of higher bonding temperature (>600 ℃) resulting in lowering obviously the joint shear strength is the widening of alumina particle segregation region that acts as a preferential site for failure. The increase of joint shear strength with increasing holding time is mainly associated with decreasing the amount of Al 2Cu brittle phase and promoting homogenization of joint.展开更多
基金Project(50475126) supported by the National Natural Science Foundation of China
文摘Plasma arc welding was used to join SiCp/Al composite with titanium as alloying filler material. Microstructure of the weld was characterized by an optical microscope. The results show that the harmful needle-like phase Al4C3 is completely eliminated in the weld of SiCp/Al metal matrix composite(MMC) by in-situ weld-alloying/plasma arc welding with titanium as the alloying element. The wetting property between reinforced phase and Al matrix is improved, a stable weld puddle is gotten and a novel composite-material welded joint reinforced by TiN, AlN and TiC is produced. And the tensile-strength and malleability of the welded joints are improved effectively because of the use of titanium.
文摘The formation process, microstructure and mechanical properties of transient liquid phase (TLP) bonded aluminium based metal matrix composite (MMC) joint with copper interlayer were investigated. The formation process of the TLP joint comprises a number of stages: plastic deformation and solid diffusion (stage 1), dissolution of interlayer and base metal (stage 2), isothermal solidification (stage 3) and homogenization (stage 4). The microstructure of the joint depends on the joint formation process (distinct stages). The plastic deformation and solid diffusion in stage 1 favoure the intimate contact at interfaces and liquid layer formation. The microstructure of joint consists of aluminium solid solution, alumina particle, Al 2Cu and MgAl 2O 4 compounds in stage 2. The most pronounced feature of joint microstructure in stage 3 is the alumina particle segregation in the center of the joint. The increase of joint shear strength with increasing bonding temperature is mainly attributed to improving the fluidity and wettability of liquid phase and decreasing the amount of Al 2Cu brittle phase in the joint. The principal reason of higher bonding temperature (>600 ℃) resulting in lowering obviously the joint shear strength is the widening of alumina particle segregation region that acts as a preferential site for failure. The increase of joint shear strength with increasing holding time is mainly associated with decreasing the amount of Al 2Cu brittle phase and promoting homogenization of joint.