The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calcul...The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.展开更多
The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the ...The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the yield strength were examined bytransmission electron microscopy （TEM） and compression tests, respectively. The results indicate that an elastic stress of 15 MPa ishigh enough to influence the precipitation distribution of θ′ during aging at 180℃. The applied stress loading along [116]Aldirection results in increased number density of θ′ on （001）Al habit planes. This result becomes more significant with increasingapplied stress and leads to lower yield strength of Al-Cu single crystals during aging. Moreover, the generation of the preferentialorientation of θ′ was discussed by the effect of the dislocation induced by applied stress as well as the role of the misfit between theθ′-precipitate and Al matrix. The results are in agreement with the effect of the latter one.展开更多
Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu...Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.展开更多
基金Project(2012CB619500)supported by the National Basic Research Program of China
文摘The precipitation kinetics of 2519 A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry（DSC）. The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy（TEM）. The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.
基金Project(51375503)supported by the National Natural Science Foundation of China
文摘The stress aging behavior of Al-Cu alloy under various applied stresses, i.e., elastic stress, yield stress and plasticdeformation stress, was investigated using single crystals. The resulting microstructures and the yield strength were examined bytransmission electron microscopy （TEM） and compression tests, respectively. The results indicate that an elastic stress of 15 MPa ishigh enough to influence the precipitation distribution of θ′ during aging at 180℃. The applied stress loading along [116]Aldirection results in increased number density of θ′ on （001）Al habit planes. This result becomes more significant with increasingapplied stress and leads to lower yield strength of Al-Cu single crystals during aging. Moreover, the generation of the preferentialorientation of θ′ was discussed by the effect of the dislocation induced by applied stress as well as the role of the misfit between theθ′-precipitate and Al matrix. The results are in agreement with the effect of the latter one.
基金Project(51301209)supported by the National Natural Science Foundation of China
文摘Transmission electron microscopy(TEM),scanning electron microscopy(SEM),hardness tests and tensile tests were performed to investigate the effect of aging on microstructure and mechanical properties of forged Al-4.4Cu-0.7Mg-0.6Si alloy.The results show that the alloy exhibits splendid mechanical properties with an ultimate tensile strength of504MPa and an elongation of10.1%after aging at170°C for16h.With tensile testing temperature increasing to150°C,the strength of the alloy declines slightly to483MPa.Then,the strength drops quickly when temperature reaches over200°C.The high strength of the alloy in peak-aged condition is caused by a considerable amount ofθ'and AlMgSiCu(Q)precipitates.The relatively stable mechanical properties tested below150°C are mainly ascribed to the stability ofθ'precipitates.The growth ofθ'and Q precipitates and the generation ofθphase lead to a rapid drop of the strength when temperature is over150°C.
基金This work is supported by Jiangsu Key Laboratory for Advanced Metallic Materials,China(No.BM2007204)the Fundamental Research Funds for the Central Universities,China(No.2242016k40011).