Spheroidizing annealing and torsion testing of 0.027 wt% carbon steel rod were conducted to evaluate spheroidization kinetic behavior at 943 K （670 ℃） under deformed and non-deformed states. Kinetic curves were als...Spheroidizing annealing and torsion testing of 0.027 wt% carbon steel rod were conducted to evaluate spheroidization kinetic behavior at 943 K （670 ℃） under deformed and non-deformed states. Kinetic curves were also predicted using the Johnson-Mehl-Avrami-Kolmogorov equation, and the results agree well with the experimental ones. After spheroidization was performed twice, the spherical cementite and precipitated carbides became smaller and the distribution was more uniform. Comparison of materials subjected to single and double spheroidizing annealing indicated a difference in grain size. Torsion performance was considerably improved under double spheroidization, especially the maximum torque with slight variations.展开更多
基金This work was supported by the National Natural Science Foundation of China （Grant No. 51271035）.
文摘Spheroidizing annealing and torsion testing of 0.027 wt% carbon steel rod were conducted to evaluate spheroidization kinetic behavior at 943 K （670 ℃） under deformed and non-deformed states. Kinetic curves were also predicted using the Johnson-Mehl-Avrami-Kolmogorov equation, and the results agree well with the experimental ones. After spheroidization was performed twice, the spherical cementite and precipitated carbides became smaller and the distribution was more uniform. Comparison of materials subjected to single and double spheroidizing annealing indicated a difference in grain size. Torsion performance was considerably improved under double spheroidization, especially the maximum torque with slight variations.